The invention relates to a slurry preparation of benzene ester plasticizers, using benzoic acid and alcohol in the presence of catalysts obtained by the reaction of benzoic acid ester plasticizer, which is characterized in that the raw material benzene acid solid granular, powder or lump in the first alcohol slurry, slurry after adjusting the molar ratio of alcohol with benzoic acid is 1 to 4: 1, and then the quality of raw materials accounted for 0.1% to benzoic acid in the reactor with oil-water separator in conventional catalyst mixing 2% after mixing gradually heated up to 210 DEG C to 240 DEG C, the reaction of 1 ~ 4 hours to less than 1 over acid reaction, then the dealcohol refined processing of benzoic acid ester plasticizer. The characteristic of this invention is not in need of comprehensive changes to the original equipment, the original solid benzene acid slurry, improving the reaction of two phases, greatly improving the reaction speed, improve efficiency and save energy consumption.
【技术实现步骤摘要】
本专利技术涉及一种浆化技术在合成苯酸类增塑剂的制备方法，具体涉及利用机械磨设备将固体原料浆化后再进行合成反应，制备增塑剂的方法。
技术介绍
众所周知，增塑剂是加工高聚物如橡胶、塑料、涂料等成型时为增加其可塑性、流动性并使成品具有柔韧性而加入的物质，是塑料工业上必不可少的添加助剂。我国年产能已达到2 800 kt，已经成为全世界第一生产和消费大国，并继续呈现增长势头。这其中邻苯二甲酸酯和对苯二甲酸酯的比例又占据了 90%以上。但研究表明邻苯类增塑剂具有潜在的致癌性，而环氧油脂和柠檬酸酯类等绿色增塑剂在产量上也难以在短期满足庞大的市场需求，所以在未来对苯类增塑剂还将是市场上的主要产品，然而传统的合成工艺耗时长，能耗尚ο
技术实现思路
为了解决现有技术存在的合成工艺耗时长、能耗高的缺点，本专利技术提供一种，先将原料浆化后再反应，反应充分、时间短。本专利技术的技术方案为一种，采用苯酸与醇在催化剂存在下反应得到苯酸酯类增塑剂，将固体颗粒状、粉状或块状的原料苯酸先在醇中浆化，浆化结束后调整醇与苯酸的摩尔比为1 4 1，然后再与占原料苯酸质量0.1% 2%的常规催化剂混合后在...
【技术保护点】
１．一种浆态法制备苯酸酯类增塑剂的方法，采用苯酸与醇在催化剂存在下反应得到苯酸酯类增塑剂，其特征在于，将固体颗粒状、粉状或块状的原料苯酸先在醇中浆化，浆化结束后调整醇与苯酸的摩尔比为１～４︰１，然后再与占原料苯酸质量０．１％～２％的常规催化剂混合后在带有油水分离器的反应器中，逐步搅拌升温至２１０℃～２４０℃，保温反应１～４小时至酸价低于１结束反应，再进行常规的脱醇、精制处理得到苯酸酯类增塑剂。
【技术特征摘要】
【专利技术属性】
技术研发人员：蒋剑春，周永红，李科，冯国东，聂小安，陈洁，许彬，陈玉湘，
申请(专利权)人：江苏强林生物能源有限公司，中国林业科学研究院林产化学工业研究所，
类型：发明
国别省市：32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。