The invention discloses a method for preparing high performance of modified asphalt, the preparation method comprises the following steps: (1) the asphalt modifier, oxidizing agent according to the weight ratio of 100:1-15:1-15 was added to the reactor, and the reaction kettle is heated to 200-300 DEG C, preparation of melt asphalt; (2) the molten asphalt prepared to spray conditioner temperature of 350-500 in the molten asphalt atomization and tempered 2-6 hours; (3) the input will melt asphalt atomization after tempering to emulsifying device temperature of 250-400 in adding emulsifier in emulsion conditioning; (4) the cooling material is more efficient to 170-200 DEG C after asphalt. The atomizing technology of the invention improves the carbon content of the asphalt, and the emulsification technique makes the porous asphalt which is easy to flow, the preparation process is simple, the time is short, the softening point of the product is low, and the comprehensive cost is low.
【技术实现步骤摘要】
本专利技术涉及浙青调制
，具体的说是一种高效改性浙青的制备方法。
技术介绍
浙青主要用于道路的铺装、维修和养护，随着技术的发展及环境保护的要求不断 提高，浙青的使用面越来越广，其中，浙青成为活性炭材料制取的一个主要原料来源，但目 前的浙青调制工艺中，特别是用以制碳制纤的浙青材料调制工艺普遍存在耗时长、能耗高 的缺点。
技术实现思路
本专利技术的目的是针对现有技术的缺陷，提供一种软化点高、耗时短、能耗低的高效 改性浙青的制备方法。本专利技术的目的是通过以下技术方案解决的一种高效改性浙青的制备方法，所述的制备方法按下述步骤进行(1)将浙青、改性剂、氧化剂按照重量比为100:1-15 :1-15的组份加入到反应釜中，并 将反应釜加热到200-300°C，配制熔融浙青；(2)将配制好的熔融浙青加入到温度为350-500°C的雾化调质塔中，对熔融浙青进行雾 化调质2-6小时；(3)将雾化调质后的熔融浙青输入到温度为250-400°C的乳化装置中，并加入乳化剂进 行乳化调质；(4)冷却降温到170-250°C以下后放料得高效浙青。所述步骤(1)中的浙青、改性剂、氧化剂按...
【技术保护点】
１．一种高效改性沥青的制备方法，其特征在于所述的制备方法按下述步骤进行：（１）将沥青、改性剂、氧化剂按照重量比为１００：１－１５：１－１５的组份加入到反应釜中，并将反应釜加热到２００－３００℃，配制熔融沥青；（２）将配制好的熔融沥青加入到温度为３５０－５００℃的雾化调质塔中，对熔融沥青进行雾化调质２－６小时；（３）将雾化调质后的熔融沥青输入到温度为２５０－４００℃的乳化装置中，并加入乳化剂进行乳化调质；（４）冷却降温到１７０－２５０℃以下后放料得高效沥青。
【技术特征摘要】
【专利技术属性】
技术研发人员：张吉太，刘明秋，邹开良，
申请(专利权)人：江苏国正新材料科技有限公司，
类型：发明
国别省市：32