The present invention provides a method for supported platinum catalyst preparation method of the fuel cell, which comprises the following steps: a) the carrier dispersed in deionized water, get the first suspension; b) adding chloroplatinic acid and formic acid to the first suspension, ultrasonic dispersion, second C) the suspension; second suspension at 10 to 40 DEG C static reaction, washing and drying to obtain the supported platinum catalyst. The invention also provides a supported platinum catalyst for a fuel cell prepared according to the method described in the above technical scheme. In the present invention, formic acid as weak reducing agent, at 10 to 40 DEG C under the condition with chloroplatinic acid reaction is slow, the generation rate of Pt atoms can be controlled, so it can become directed generation of nanowires, which has high catalytic activity and high utilization rate of Pt. The method provided by the invention has simple operation and mild condition.
【技术实现步骤摘要】
本专利技术属于燃料电池
，尤其涉及一种用于燃料电池的负载型钼催化剂及 其制备方法。
技术介绍
燃料电池是通过电化学反应将燃料所含化学能直接、连续地转化为电能的高效、 洁净的发电系统，包括质子交换膜燃料电池(PEMFC)、熔融碳酸盐燃料电池(MCFC)和固体 氧化物燃料电池(SOFC)等。其中，质子交换膜燃料电池具有运行温度低、能量密度高、无腐 蚀、启动快等优点在便携式电源和小型电源等方面具有良好的应用前景。在质子交换膜燃料电池中，催化层是电极进行电化学反应的场所，催化层的结构、 催化剂的活性和稳定性对电池的性能均有重要影响。由于金属钼价格昂贵且资源有限，目 前燃料电池常用的催化剂为负载型钼催化剂，即将钼负载在载体上形成的复合催化剂。负 载型钼催化剂的催化性能与催化剂的本征物理化学性能有关，如纳米钼金属粒径大小、纳 米钼金属粒子在碳上的分散程度、物相和化学组成、杂质的影响等，其中，一维纳米线结构 由于具有各向异性结构造成优势晶面暴露等优点，用作燃料电池的催化剂时能够提高钼的 利用率。现有技术公开了多种纳米线结构的负载型钼催化剂，如Jimg等采用模板法 合成了...
【技术保护点】
１．一种用于燃料电池的负载型铂催化剂的制备方法，包括以下步骤：ａ）将载体分散于去离子水中，得到第一悬浊液；ｂ）向所述第一悬浊液中加入氯铂酸和甲酸，超声分散后，得到第二悬浊液；ｃ）将所述第二悬浊液在０℃～４０℃静置反应，洗涤、干燥后得到负载型铂催化剂。
【技术特征摘要】
【专利技术属性】
技术研发人员：刘长鹏，司凤占，严亮，冯立纲，张新波，邢巍，
申请(专利权)人：中国科学院长春应用化学研究所，
类型：发明
国别省市：82