用于油烟分离及油汽分离的过滤材料制造技术

本发明专利技术提供了一种用于油烟分离及油汽分离的过滤材料，呈三维网状多孔结构，以铁、镍、铜或其合金金属构成骨架基材，在基材骨架的网格肋条上有枝状结晶凸起；过滤材料的孔隙率为95％～99％，孔径为10～120PPI，并且0.1≤过滤材料的密度＜0.2g/cm3。本发明专利技术的过滤材料在确保机械强度的条件下，其密度可以更低，一方面既可减少过滤器重量，另一方面也可以降低材料成本；并且本发明专利技术的过滤材料的净化效率也有明显提高。

Filter material for oil fume separation and oil vapor separation

The invention provides a filter material for oil fume separation and oil vapor separation, a three-dimensional porous network structure, iron, nickel, copper or copper alloy metal substrate on the substrate to form the framework, the skeleton grid ribs have dendritic crystal bulges; filter material porosity is 95% ~ 99%, the diameter of 10 to 120PPI less than 0.1, and the filter material density is less than 0.2g/cm3. The filter material of the invention in ensuring the mechanical strength under the condition that the density is lower, on the one hand can reduce the weight of the filter, on the other hand can also reduce the material cost; and the purification efficiency of filter material of the invention can be improved significantly.

【技术实现步骤摘要】

本专利技术涉及一种过滤材料，特别涉及一种用于油烟分离及油汽分离的过滤材料。
技术介绍
目前在厨房油烟分离净化及工业油汽分离用过滤器中的过滤材料基本采用多孔陶瓷材料及金属纤维毡，多孔陶瓷及金属纤维毡等材料存在重量大，安装拆卸不方便；捕集效率低，风阻大；特别陶瓷过滤材料耐冲击须性能差，使用或拆卸清洗过程中因碰撞或跌落易导致破损失效。而日本专利3303395B2提出将泡沫镍金属材料应用于厨房油烟净化，要求比重为0. 2 0. 7，该专利所提出的产品可有效提高油烟的净化效率，降低产品的重量及失效风险。但其仅限于多孔金属镍，而且为了保持材料的机械强度，要求产品密度较高，且这种材料的骨架肋条表面光滑，粗糙度不够，油烟的捕集效率仍较低，为提高捕集效率需加后泡沫金属过滤层的厚度，从而导致金属使用量增加，使得过滤器的成本升高。
技术实现思路
本专利技术旨在提供一种可保证机械强度的情况下具有较低比重、耐高温耐腐蚀性能良好、成本低廉的油烟分离及油汽分离用过滤器中的过滤材料。本专利技术通过以下方案实现用于油烟分离及油汽分离的过滤材料，呈三维网状多孔结构，以铁、镍、铜或其合金金属构成骨架基材，在基材骨架的网格本文档来自技高网...

【技术保护点】
１．一种用于油烟分离及油汽分离的过滤材料，其特征在于：呈三维网状多孔结构，以铁、镍、铜或其合金金属构成骨架基材，在基材骨架的网格肋条上有枝状结晶凸起；过滤材料的孔隙率为９５％～９９％，孔径为１０～１２０ＰＰＩ，并且０．１≤过滤材料的密度＜０．２ｇ／ｃｍ３。

【技术特征摘要】

【专利技术属性】
技术研发人员：蒋素斌，谢红雨，朱济群，俞钧，洪志刚，谭水发，肖鑫，周小平，阳保国，李秀琴，邹超，冯金桥，
申请(专利权)人：长沙力元新材料有限责任公司，
类型：发明
国别省市：43