一种造船用热轧钢卷的生产方法技术

本发明专利技术涉及一种造船用热轧钢卷的生产方法，包括：1)成分设计，对铁水进行预处理，然后转炉冶炼，氮氩切换，出钢得钢水；2)将上述钢水进行连铸得板坯，连铸中包停浇时中包钢水量控制在8～15t，液位200～350mm；全程保护浇注，长水口插入深度300～400mm；3)将上述的板坯加热；4)最后将上述加热后的板坯轧制，卷曲即得。本发明专利技术降低了E级钢成分中C、Mn含量，采用合适的轧制工艺及控冷工艺，提高E级钢的综合性能，生产出低成本、高性能的E级热轧钢卷。

Method for producing hot-rolled steel coil for shipbuilding

Including the method of the present invention relates to a production for shipbuilding steel coils: 1) composition design of hot metal pretreatment, and smelting, nitrogen and argon switching, tapping to molten steel; 2) the continuous casting of molten steel in tundish to slab casting stop in Baotou water control in 8 ~ 15t level 200 ~ 350mm; full protection casting, long nozzle insertion depth of 300 ~ 400mm; 3) heating the slab; 4) will be the last slab rolling after heating, the crimp. The invention reduces the content of C and Mn in the composition of E grade steel, improves the comprehensive performance of E grade steel by proper rolling process and cooling control process, and produces E grade hot-rolled steel coil with low cost and high performance.

【技术实现步骤摘要】

本专利技术属于热轧钢卷制备领域，特别涉及。
技术介绍
现生产的屈服强度235MI^级系列钢卷成分中C高，铸坯表面裂纹多，强度富余量 大，塑性及韧性低。专用钢中对Mn的下限有要求时，其强度富余量将更大，影响冷加工性 能；铸坯表面有裂纹几率大不能直装，不利于节能减排；含C量高，焊接性能差。屈服强度235MPa级系列钢卷生产性能实绩调查表1屈服强度235MPa级系列钢卷厚度、性能范围统计表权利要求1.，包括1)成分设计好后，对铁水进行预处理，然后转炉冶炼，氮氩切换，出钢得钢水，出钢前补 吹彡1次，出钢时间4. 5 8. Omin ；出钢4/5前加完合金；出钢双挡渣，到站渣厚彡80mm ； 氩站处理吹氩全程时间17 30min ；其中所述钢水各成分的重量百分比依次为C0. 05 0. 08%, Si 0. 12 0. 24%，MnO. 80 0. 90%，P < 0. 020%，S < 0. 020%，Als 0.020% 0. 040%，其余为铁和不可避免的杂质；2)将上述出钢后的钢水进行连铸得板坯，其中连浇第一炉中包开浇时中包钢水量 25 30t，液位550 58本文档来自技高网...

【技术保护点】
１．一种造船用热轧钢卷的生产方法，包括：１）成分设计好后，对铁水进行预处理，然后转炉冶炼，氮氩切换，出钢得钢水，出钢前补吹≤１次，出钢时间４．５～８．０ｍｉｎ；出钢４／５前加完合金；出钢双挡渣，到站渣厚≤８０ｍｍ；氩站处理吹氩全程时间１７～３０ｍｉｎ；其中所述钢水各成分的重量百分比依次为：Ｃ０．０５～０．０８％，Ｓｉ　０．１２～０．２４％，Ｍｎ０．８０～０．９０％，Ｐ≤０．０２０％，Ｓ≤０．０２０％，Ａｌｓ　０．０２０％～０．０４０％，其余为铁和不可避免的杂质；２）将上述出钢后的钢水进行连铸得板坯，其中连浇第一炉中包开浇时中包钢水量２５～３０ｔ，液位５５０～５８０ｍｍ；中包快换时中包钢水量１５...

【技术特征摘要】

【专利技术属性】
技术研发人员：杨云清，曹太平，丘祥光，石鸿，蒋鲜林，朱凯，张庆雨，
申请(专利权)人：宁波钢铁有限公司，
类型：发明
国别省市：97