The invention relates to a production method, a kind of hot rolled steel coil includes: 1) composition design of hot metal pretreatment, and smelting, nitrogen and argon switching, tapping to just water; 2) the continuous casting of molten steel in tundish to slab casting stop in Baotou water control in 8 ~ 15t level. 200 ~ 350mm; full protection casting, long nozzle insertion depth of 300 ~ 400mm; 3) heating the slab; 4) will be the last slab rolling after heating, the crimp. The invention adopts the TMCP+RPC rolling process, the content of niobium microalloying to reduce C and Mn, reduce the production cost; the invention of the Q345D hot rolled steel roll has excellent plasticity and toughness, the elongation rate increased by more than 8%, while improving the performance of welding materials, ensure the quality of continuous casting billet surface.
【技术实现步骤摘要】
本专利技术属于钢卷制备领域，特别涉及。
技术介绍
现生产屈服强度345MPa级系列钢卷各钢厂成分中C高，铸坯表面裂纹多，强度富 余量大，塑性及韧性低。强度富余量大，影响冷加工性能；铸坯表面有裂纹几率大不能直装， 不利于节能减排；含C量高，焊接性能差；钢中Mn含量高，生产成本居高不下，产品市场竞 争能力差；轧钢采用任意轧制工艺，产品的性能波动范围大，不利于用户的使用。Q345系列钢卷生产性能实绩调查表1 Q345系列钢厚度、性能范围统计表权利要求1.，包括1)成分设计好后，对铁水进行预处理，然后转炉冶炼，氮氩切换，出钢得钢水；出钢 前补吹彡1次，出钢时间4. 5 8. Omin ；出钢4/5前加完合金；出钢双挡渣，到站渣厚 ^ 80mm ；氩站处理吹氩全程时间17 30min ；其中所得钢水各成分的重量百分比依次为 CO. 06 0. 08 %，Si 0. 20 0. 30 %，Mn 0. 60 0. 80 %，P 彡 0. 020 %，S 彡 0. 015 %， Nb+Ti+V^ 0. 060%, Als 0. 020 0. 035%，其余为铁和不可避免...
【技术保护点】
１．一种热轧钢卷的生产方法，包括：１）成分设计好后，对铁水进行预处理，然后转炉冶炼，氮氩切换，出钢得钢水；出钢前补吹≤１次，出钢时间４．５～８．０ｍｉｎ；出钢４／５前加完合金；出钢双挡渣，到站渣厚≤８０ｍｍ；氩站处理吹氩全程时间１７～３０ｍｉｎ；其中所得钢水各成分的重量百分比依次为：Ｃ０．０６～０．０８％，Ｓｉ ０．２０～０．３０％，Ｍｎ ０．６０～０．８０％，Ｐ≤０．０２０％，Ｓ≤０．０１５％，Ｎｂ＋Ｔｉ＋Ｖ≤０．０６０％，Ａｌｓ ０．０２０～０．０３５％，其余为铁和不可避免的杂质；２）将上述出钢后的钢水进行连铸得板坯，其中连浇第一炉中包开浇时中包钢水量２５～３０ｔ，液位...
【技术特征摘要】
【专利技术属性】
技术研发人员：杨云清，曹太平，贾国军，丘祥光，赵彦灵，于长春，吴伟娟，张军霞，
申请(专利权)人：宁波钢铁有限公司，
类型：发明
国别省市：97