The invention belongs to the refractory material field of a dry coke quenching device, in particular to a mullite andalusite product at a key part of a CDQ device and a method for making the same. Characterized by the number of copies than the quality of following raw materials: M60 mullite particles 10 - 15; M47 mullite particles 40 ~ 55; 10 to 15 parts of andalusite sillimanite; pickling 10 - 15; alpha AL2O3 powder 5 - 10; 5 - 10 with clay pulp; 3 - 5 bond. The raw materials are mixed, processed, separated by magnetic separation, treated with iron and sieved, and then put into a molding machine to be pressed. After the molding, the semi-finished products are dried and then burned into the kiln to make finished products. The present invention has the advantages of good thermal shock resistance, good thermal expansion rate, small elastic modulus and good thermal shock resistance.
【技术实现步骤摘要】
本专利技术属于干法熄焦装置用耐火材料领域,具体涉及一种干熄焦装置关键部位用莫来石-红柱石制品及其制法。
技术介绍
干法熄焦装置是国家发改委启动的十大节能工程之一,具有环保、节能、提高焦炭质量等优点。自2000年6月国家经贸委正式批复将“干熄焦技术开发列为国家重大引进消化吸收“一条龙”攻关”开发项目后,武钢焦化厂于2002年上马了国内首座引进消化吸收的 140t/hr大型的干熄焦装置。近几年来国内相继建设了大量的干熄焦装置,其中早期关键部位设计均采用了 A级莫来石-SiC材质(简称AT),其技术指标如下权利要求1.一种干熄焦装置关键部位用莫来石-红柱石制品,其特征在于所采用原料的质量份数比如下M60莫来石颗粒10-15份; M47莫来石颗粒40 55份; 红柱石10-15份; 酸洗硅线石10-15份; α -AL2O3 微粉 5-10 份; 结合粘土 5-10份; 纸浆结合剂3-5份。2.根据权利要求1所述的干熄焦装置关键部位用莫来石-红柱石制品的制法,其特征在于所采用的原料质量如下Μ60莫来石颗粒10-15份,Μ47莫来石颗粒40 55份,红柱石 10-15份,酸洗硅线石10-15份,α -AL2O3微粉5_10份,结合粘土 5_10份,纸浆结合剂3_5 份。制备方法步骤如下(1)配制混合粉先将红柱石、酸洗硅线石、α-AL2O3微粉和结合粘土按质量份数比准确称量送入混合机中进行预混合均勻,混练10-15分钟;(2)Μ60莫来石颗粒料筛分为3-lmm规格,Μ47莫来石颗粒料筛分为3-1、彡1和彡0.5mm 三种规格,以上规格料经磁选机进行磁选除铁;(3)将 ...
【技术保护点】
1.一种干熄焦装置关键部位用莫来石-红柱石制品,其特征在于所采用原料的质量份数比如下:M60莫来石颗粒10-15份;M47莫来石颗粒40~55份;红柱石10-15份;酸洗硅线石10-15份;α-AL2O3微粉5-10份;结合粘土5-10份;纸浆结合剂3-5份。
【技术特征摘要】
【专利技术属性】
技术研发人员:刘伟,李文亮,蔡国庆,王希波,刘成强,燕宿祥,
申请(专利权)人:山东鲁耐窑业有限责任公司,
类型:发明
国别省市:37[]