Aromatic polyether glycidyl ether epoxy resin and preparation method thereof

The invention relates to an epoxy resin and a preparation method thereof, in particular to an aromatic polyether glycidyl ether epoxy resin with high toughness after curing and a preparation method thereof. The invention relates to an aromatic polyether glycidyl ether epoxy resin with the following structure by reacting an aromatic polyether with an epoxy chloropropane. The aromatic polyether glycidyl ether epoxy resin has the advantages of low viscosity and good processing performance. It can be used alone as an epoxy resin or as a toughening modifier for other epoxy resins. When used alone as the epoxy resin, curing the aromatic polyether glycidyl ether epoxy resin has excellent toughness; when other toughening epoxy resin as modifier is used, the other can greatly improve the toughness of epoxy resin, and epoxy resin, reduce the tensile bending strength and heat resistance.

【技术实现步骤摘要】

本专利技术涉及环氧树脂及其制备方法，特别涉及固化后具有高韧性的。
技术介绍
环氧树脂由于具有良好的粘接性、力学强度、耐化学腐蚀性以及工艺性能等优点，在胶黏剂、涂料、微电子封装和复合材料基体等领域有着非常广泛的应用。但是常用的环氧树脂如双酚A环氧树脂固化后都存在冲击强度低，脆性大的缺点，在实际应用中经常需要对环氧树脂进行增韧。常见的增韧方法是在环氧树脂的基体中加入橡胶弹性体、 无机刚性粒子或热塑性塑料等第二组分与环氧树脂的基体形成分相结构，通过弹性体颗粒吸收能量或相分离诱导界面处环氧塑性变形提高环氧树脂的韧性(如文献European PolymerJournal. V38,2002,251-264 ；Polymer. V41,2000,4451-4459 ；Polymer.V48,2007, 530-541等报道)，或者采用与环氧树脂具有一定相容性的超支化聚酯或嵌段共聚物等韧性较好的高聚物加入环氧树脂中形成半/全互穿网络结构使环氧树脂增强增韧(如Polym. Adv. Technol. V19, 2008，1597-1607 ；Macromo 1. Symp. 2007，256，55本文档来自技高网...

【技术保护点】
１．一种芳香族聚醚缩水甘油醚环氧树脂，其特征是，所述的树脂具有以下结构：其中：Ｒ为

【技术特征摘要】

【专利技术属性】
技术研发人员：黄伟，杨欣，赵晓娟，张瑛，余云照，
申请(专利权)人：中国科学院化学研究所，
类型：发明
国别省市：11[]