一种新型银基电接触弹性材料及其应用制造技术

本发明专利技术公开了一种新型银基电接触弹性材料及其应用。所述材料包含下列成分：0.35wt％～1.0wt％的Ni，4wt％～10wt％的Cu，0.001wt％～0.1wt％的Mg、Zn、Y中的一种或两种以上元素，其余量为Ag。本发明专利技术涉及的银基电接触材料在250℃下仍保持良好的弹性及高温强度，材料的接触电阻低，抗熔焊、抗电弧侵蚀能力强。该新型银基电接触材料可在轻、中负荷条件下作为热敏熔断器弹性触点材料使用，可有效防止触点发生熔焊、粘连等现象，使材料使用寿命延长、可靠性提高。

A new type of silver based electrical contact elastic material and its application

The present invention discloses a new silver base electric contact elastic material and its application. The material comprises the following components: 0.35wt% to 1.0wt%, 4wt% to 10wt%, 0.001wt%, 0.1wt%, Mg, Zn, Y, one or more than two elements in Cu, and the remaining quantity is Ag (Ni). The silver based electrical contact material of the present invention still has good elasticity and high temperature strength at 250 DEG C, the contact resistance of the material is low, and the welding resistance and arc erosion resistance are strong. The new silver based electrical contact material can be used as a thermal fuse elastic contact material in the light, in the load condition, which can effectively prevent the occurrence of contact welding, such as adhesion phenomenon, the material and prolong the service life and reliability improvement.

【技术实现步骤摘要】

本专利技术涉及金属材料领域，特别是涉及一种新型银基电接触弹性材料及其应用。
技术介绍
银基电接触材料由于其接触电阻低、抗熔焊能力强、耐磨损性能良好、抗电侵蚀能 力强等特点近年来得到飞速发展，研究和开发的电接触材料主要包括纯银、银基固溶体合 金、银金属间化合物、银氧化物材料、银非氧化物复合材料等，主要应用于接触器、电位器、 继电器、断电器等电转换装置中。目前，电接触材料的制备方法主要有合金化法、粉末冶金 法、内氧化法等。随着电子电力元器件不断小型化、高精度、高可靠方向的发展，对于一些特殊环境 下使用的电接触材料，不仅要求材料具有低的接触电阻，抗熔焊、抗电弧侵蚀能力强，同时 要求电接触材料具有良好的耐高温性能，在较高温度下仍保持高的强度和弹性。但用目前 方法制备的银基电接触材料在较高温度如250°C工作时，容易发生熔焊、粘连等问题，从而 影响元器件的使用寿命和可靠性。因此，为了满足电子电力元器件不断发展的需要，需研究开发一种新型银基电接 触弹性材料，其不仅具有接触电阻低，抗熔焊、抗电弧侵蚀能力强的特点，且其在250°C工作 时材料仍保持良好的弹性和热稳定性，该材料具有可加工成极小尺寸本文档来自技高网...

【技术保护点】
１．一种银基电接触弹性材料，其特征在于：以重量百分比计，含有下列成分：０．３５ｗｔ％～１．０ｗｔ％的Ｎｉ，４ｗｔ％～１０ｗｔ％的Ｃｕ，０．００１ｗｔ％～０．１ｗｔ％的Ｍｇ、Ｚｎ、Ｙ中的一种或两种以上元素，余量为Ａｇ。