Controllable preparation and application of the invention belongs to the technical field of nano materials, in particular to use prepared by hydrothermal method and the magnetic properties of Fe: 3 O: 4 polymer sub micrometer sphere and magnetic Fe: 3 O: 4 polymer submicrospheres. The invention uses ferric salts as iron source, using polymer dextran, chitosan and polyacrylic acid as surfactant by hydrothermal method can be obtained in step 3: Fe magnetic O: 4 ball coated dextran magnetic Fe: 3 O: 4 polymer submicrospheres surface coating of chitosan magnetic Fe: 3 O: 4 polymer sub micrometer sphere, or surface of polyacrylic acid coated magnetic Fe: 3 O: 4 polymer submicrospheres. According to the different functional groups of these polymers, different functional molecules can be combined to achieve different biological applications. Three kinds of polymer, the magnetic properties of Fe: 3 O: 4 sub micron ball size, uniformity and monodispersity can better control the reaction conditions, ball size between 200 ~ 1000nm.
【技术实现步骤摘要】
本专利技术属于纳米材料的可控制备和应用
，特别涉及用水热法制 备得到的多功能磁性Fe304聚合物亚微米球及磁性Fe304聚合物亚微米球的用途。
技术介绍
磁性纳米材料因具有强磁性和低细胞毒性在生物医学上有巨大的应用潜 力，如在抗体和融合蛋白的纯化、药物或基因的投递、免疫检测和磁共振成 像等方面都有广泛的应用。但是，单纯的磁性纳米材料在生物医学上的应用 存在着严重的缺陷，因此，近年来磁性纳米材料的多功能化因思路新颖和用 途广泛成为研究热点，它具有集主动靶向、成像、低细胞毒性和治疗等于一 身的优势。无机材料存在分散性好、尺寸和形貌易控以及均一性好等在可控 性上的优势，有机材料具有毒性小、体内可降解和易于多功能化等在应用性 上的优势，因此结合两者的长处构建新的多功能磁性材料将弥补相互间的不 足和拓展在生物医学上的应用。相对于一般纳米颗粒的制备而言，多功能聚合物磁性纳米球颗粒的制备 难度较大，往往需要较为繁琐的制备流程，使得材料表面所带功能团量比较 少，影响材料多功能化的目的，进而削弱材料在生物医学上的应用。目前， 已报道的制备多功能化聚合物磁性纳米球颗粒的方法主...
【技术保护点】
一种用水热法制备得到的磁性Ｆｅ↓［３］Ｏ↓［４］聚合物亚微米球，其特征是，该磁性Ｆｅ↓［３］Ｏ↓［４］聚合物亚微米球是由以下方法制备得到的： １）配制三价铁盐的乙二醇溶液，浓度为０．０１～０．５ｍｏｌ／Ｌ； ２）向步骤１）得到溶 液中加入无水醋酸钠，使无水醋酸钠的终浓度为０．０５～１０ｍｏｌ／Ｌ； ３）向步骤２）得到溶液中加入葡聚糖、壳聚糖或聚丙烯酸，使葡聚糖、壳聚糖或聚丙烯酸的终浓度为０．０５～１００ｍｇ／ｍｌ； ４）将步骤３）得到的混合物置于密闭的反 应釜中，在１００～２５０℃下进行反应，反应时间为５～５０小时；得到在磁性Ｆｅ...
【技术特征摘要】
【专利技术属性】
技术研发人员：唐芳琼，黄兴禄，陈东，
申请(专利权)人：中国科学院理化技术研究所，
类型：发明
国别省市：11[中国|北京]