The invention discloses a PVC special filler nanometer calcium carbonate with thermal stability function of the industrialized preparation method, which comprises the following steps: (1) in the carbonization to pH for 6.5 ~ 7 nanometer calcium carbonate suspension, adding zinc salt under stirring, adding to the Zinc Oxide measure, is the weight of nano calcium carbonate from 0.5 to 1.5%; (2) calcium carbonate slurry adding zinc salt is heated to 6085 DEG C, adding stearic acid emulsion saponification and emulsification, constant temperature in the pump under the coating treatment for 1 to 2 hours, the pulp after coating; (3) the coated pulp after filtration until water content is less than 55% of the cake, at 80 to 110 DEG C drying, is obtained for PVC with the function of thermal stability of nano calcium carbonate functional filler. In the processing of PVC, the product not only acts as a filler for toughening and reinforcing, but also has better thermal stability.
【技术实现步骤摘要】
本专利技术涉及一种PVC专用具有热稳定性功能填料纳米碳酸钙的工业化制 备方法，具体的说是在纳米碳酸钙的表面均匀包覆一层PVC专用转锌复合稳定剂的工业化制备方法。
技术介绍
聚氯乙烯(PVC)是世界上用量较大的合成树脂之一，具有质轻、强度高、 阻燃、耐腐蚀、绝缘、透明等特点。PVC在100-15(TC下开始明显分解，紫外 光、机械力、氧、臭氧、氯化氢以及活性金属离子等都会大大加速PVC的分 解。PVC的热氧老化较复杂，往住同时进行好几种化学反应过程。既有分解 脱氯化氢，又有氧化断链与交联，此外还有少量芳构化和大分子链断裂生成 烃的反应过程，其中分解脱氯化氢是导致PVC老化的主要原因。在聚氯乙烯结构中，内部的烯丙基氯最不稳定，依次是叔氯、末端烯丙基氯、仲氯。从 这一点出发，聚氯乙烯降解最初是由于脱掉一个氯化氢而引起的。脱氯化氢 是在分子上含有或相邻于叔氯或烯丙基氯的某一点上开始，不管是叔氯还是 烯丙基氯都能起到一个活化基团的作用。脱掉一个氯化氢分子随即在聚氯乙 烯树脂键形成一个不饱和双键，于是就使相邻的氯原子活化。这个氯原子在 结构上和烯丙基氯一样，这就促使另一个...
【技术保护点】
一种ＰＶＣ专用具有热稳定性功能填料纳米碳酸钙的工业化制备方法，其特征在于，依次包括如下步骤： （１）在碳化至ｐＨ为６．５～７的纳米碳酸钙悬浮液浆料中，在搅拌下加入可溶性锌盐，加入量以氧化锌计量，是纳米碳酸钙重量的０．５～１．５％； （２）将加入锌盐的碳酸钙浆料升温至６０－８５℃后，加入经皂化的硬脂酸乳液，恒温并在乳化泵的分散下包覆处理１～２小时，得包覆后的浆料； （３）将包覆后的浆料过滤至含水量小于５５％的滤饼，在８０～１１０℃烘干，即获得用于ＰＶＣ的具有热稳定性功能的纳米碳酸钙功能性填料。
【技术特征摘要】
【专利技术属性】
技术研发人员：顾达，姚成，李燕，邓丽丽，王旭辉，
申请(专利权)人：上海卓越纳米新材料股份有限公司，
类型：发明
国别省市：31[中国|上海]