本发明专利技术涉及一种用于生产载带的原料，其特征在于：所述的聚苯乙烯原料的配方重量百分比为：聚苯乙烯１０－５０％、聚碳酸酯４０－８０％、相容剂３－９％、硬脂酸钙０．０３－０．０７％、抗氧剂０．１－０．５％和抗静电剂２－８％，上述各原料成分的重量百分比之和为１００％。通过上述配方的改进，可以实现聚苯乙烯原料的增韧改性并使其具有一定的抗静电性能，同时由于ＰＣ和ＰＳ的折光指数较接近，所以制得的聚苯乙烯原料可以保持较好的透明性。

Polystyrene raw material for producing carrier band and production process thereof

The invention relates to a method for producing carrier material, which is characterized in that: the formula of the weight percentage of polystyrene raw material: Polystyrene 10 - 50%, 40 - 80% polycarbonate compatibilizers, 3 - 9%, 0.03 - 0.07% of calcium stearate and antioxidant 0.1 - 0.5% and 2 - 8% antistatic agent, the composition of raw material the weight percentage and 100%. Through the improvement of the above formula, can realize the toughening modification of polystyrene material which has certain antistatic properties, at the same time as the PC and PS of the refractive index is close, so the prepared polystyrene raw material can maintain good transparency.

【技术实现步骤摘要】

【技术保护点】
一种用于生产载带的聚苯乙烯原料，其特征在于：所述的聚苯乙烯载带的配方重量百分比为：聚苯乙烯１０－５０％、聚碳酸酯４０－８０％、相容剂３－９％、硬脂酸钙０．０３－０．０７％、抗氧剂０．１－０．５％和抗静电剂２－８％，上述各原料成分的重量百分比之和为１００％。

【技术特征摘要】

【专利技术属性】
技术研发人员：吕静，许乾慰，王国建，吕世斗，
申请(专利权)人：上海虹权新材料科技有限公司，
类型：发明
国别省市：31[中国|上海]