一种丙烯酸超支化树脂，由重量分数５０－７０％的单官能度乙烯基单体、重量分数２０－４０％的双官能度乙烯基单体和重量分数５－１０％的含双键钛酸酯偶联剂通过原子转移自由基聚合法共聚获得。将单官能度乙烯基单体和双官能度乙烯基单体和含双键的钛酸酯偶联剂一起进行共聚，使得该树脂具有干燥速度快、硬度高、耐水性好、耐盐雾性能好、耐腐蚀性好、附着力佳等优异性能。而且，镜背漆为淋涂施工，由于本体系中只有一种树脂，不会出现断幕、气泡等影响施工的情况。

Hyperbranched acrylic resin and its application in mirror coating

A kind of hyperbranched acrylic resin, the weight fraction of 50 - 70% mono functional vinyl monomer, 20 - 40% weight fraction of difunctional vinyl monomer and the weight fraction of 5 - 10% titanate coupling agent containing double bond polymerization copolymerization obtained by atom transfer radical. The mono functional vinyl monomer and difunctional vinyl monomers were copolymerized together and titanate coupling agent containing double bonds, so that the resin has high drying speed, high hardness, good water resistance, salt fog resistance, good corrosion resistance, good adhesion and excellent performance. In addition, the back coating is made of spraying coating. Because there is only one kind of resin in the system, it will not affect the construction.

【技术实现步骤摘要】

本专利技术涉及一种超支化树脂，尤其涉及一种丙烯酸超支化树脂，以及作为主要组分应用镜背涂料中。
技术介绍
根据镜子所用金属材料不同，可分为铝镜和银镜两种。铝镜即是在玻璃背面真空溅射铝膜为反射层；银镜则通过化学方法先在玻璃表面镀一层金属银作为反射层，然后再在银膜上镀一层铜，以增加银膜的反射效果并起到保护银膜作用。无论采用哪种工艺，最后都需要在金属层表面再涂覆保护涂料，又称镜背漆。 镜背漆要求具有优良的施工性能，即快速固化(快干)以适应流水线生产，幕帘稳定已保证可以淋涂施工。同时还要求其有优良的防腐蚀性能(如二甲苯溶剂)，在浴室及卫生间的高温高湿和强腐蚀性环境(如FeCl3溶液、H2S气体和盐雾等)下能保护镜子背面的金属反射层。 中国专利技术专利申请00812016.1公开了一种玻璃的涂层，涂层采用含有有机硅烷胶的醇酸树脂涂料或含有氨基树脂和有机硅烷胶的醇酸树脂涂料。这类涂料虽然在烘干速度和硬度方面有了提高，但柔韧性、附着力和耐久性方面仍存在缺陷。如镜子使用一段时间后，涂层发生脱落，尤其在镜子的切口部位会发黑，使镜子的光学性能下降。另一方面，有机硅烷的价格较贵，使用成本亦较高。本文档来自技高网...

【技术保护点】
一种丙烯酸超支化树脂，其特征在于包括重量分数５０－７０％的单官能度乙烯基单体和重量分数２０－４０％的双官能度乙烯基单体和重量分数５－１０％的含双键钛酸酯偶联剂。

【技术特征摘要】

【专利技术属性】
技术研发人员：包柏青，周加祥，杨二霞，
申请(专利权)人：江苏柏鹤涂料有限公司，江苏柏鹤化工集团，
类型：发明
国别省市：32[中国|江苏]