一种低粘无光膜漆及其制备方法技术

本发明专利技术涉及一种低粘无光膜漆及其制备方法，该低粘无光膜漆包括以下组分及含量：芳香烃４０～８０ｗｔ％，低分子量酯５～３０ｗｔ％，酮类５～３０ｗｔ％，硝化纤维素１～１０ｗｔ％。与现有技术相比，本发明专利技术具有不影响荧光材料的发光性能，可形成连续、致密光滑的涂层，可有效保护荧光涂层，洁净度高、金属含量少等特点。

Low viscosity non light film paint and preparation method thereof

The invention relates to a low viscosity without light paint film and its preparation method, the low viscosity without light paint film comprises the following components and contents of aromatic hydrocarbons: 40 ~ 80wt%, 5 ~ 30wt% of low molecular weight esters, ketones 5 ~ 30wt%, 1 ~ 10wt% of nitrocellulose. Compared with the prior art, the invention has no influence on the luminescent property of the fluorescent material, and can form a continuous, dense and smooth coating, which can effectively protect the fluorescent coating, and has the characteristics of high cleanness and little metal content.

【技术实现步骤摘要】

本专利技术涉及无光膜漆，具体涉及。
技术介绍
现有低粘无光膜漆产品基本依赖进口，其用途为减少进行屏玻璃的三色镀 膜时产生的释放气体量，有利于提高发光亮度，防止涂敷劣化，使后序中涂敷 铝膜更为平整，而现有的低粘无光膜漆并不能很好的减少进行屏玻璃的三色镀 膜时产生的释放气体量，提高发光亮度，而且易导致涂敷裂化，使涂层凸凹不 平。
技术实现思路
本专利技术的目的就是为了克服上述现有技术存在的缺陷而提供一种可形成 连续、致密光滑的涂层，可有效保护荧光涂层，洁净度高、金属含量少的低粘 无光膜漆及其制备方法。本专利技术的目的可以通过以下技术方案来实现 一种低粘无光膜漆，其特征 在于，该低粘无光膜漆包括以下组分及含量芳香烃40 80wt^，低分子量酯 5~30wt%，酮类5 30wtX，硝化纤维素1 10 wt%。所述的芳香烃包括苯、甲苯、二甲苯。所述的低分子量酯包括乙酸乙酯、乙酸丁酯、乙酸异戊酯、苯甲酸甲酯。 所述的酮类包括丙酮、苯乙酮、环己酮、甲乙酮、甲基乙丁酮。 所述的硝化纤维素为粘度小于800的低粘硝化纤维素。 一种低粘无光膜漆的制备方法，其特征在于，将芳香烃加入反应釜，调制 搅拌器转速；本文档来自技高网...

【技术保护点】
一种低粘无光膜漆，其特征在于，该低粘无光膜漆包括以下组分及含量：芳香烃４０～８０ｗｔ％，低分子量酯５～３０ｗｔ％，酮类５～３０ｗｔ％，硝化纤维素１～１０ｗｔ％。

【技术特征摘要】

【专利技术属性】
技术研发人员：吉玉金，金重万，杨陈，
申请(专利权)人：上海在然化工有限公司，
类型：发明
国别省市：31[中国|上海]