一种耐磨耐碱耐火浇注料的制备方法技术

本发明专利技术公开了一种具有耐磨性、耐碱侵蚀性、耐冲刷性优异的新型耐火浇注料，即一种耐磨耐碱耐火浇注料的制备方法。采用本发明专利技术方法配制的耐磨耐碱耐火浇注料在经过３小时１１００℃烧后耐磨性低于３．５／ｃｍ↑［３］，耐碱性达到一至二级。在大型水泥窑三次风管弯头、风阀、篦冷机喉部、矮墙等部位使用，与目前使用的耐火材料相比，其耐磨性好，同时具有优异的耐碱侵蚀性，可大大提高水泥窑运转率。

Preparation method of wear-resistant alkali resistant refractory castable

The invention discloses a new refractory castable, which has the advantages of abrasion resistance, alkali resistance, erosion resistance and erosion resistance, and is a preparation method of a wear-resistant alkali resistant refractory castable. Wear resistant alkali resistant refractory castable prepared by the method of the material after 3 hours of 1100 DEG C burning resistance less than 3.5 / cm = 3, alkali resistance reached to level two. The use of a large cement kiln three wind pipe bend, air valve, cooler throat, wall and other parts, compared with refractory materials used at present, its good wear resistance, and excellent alkali erosion resistance, can greatly improve the operation rate of the cement kiln.

【技术实现步骤摘要】

【技术保护点】
一种耐磨耐碱耐火浇注料的制备方法，其特征在于：耐磨耐碱耐火浇注料的制备方法是由原料配比和制作工艺组成，其原料配比按下列重量％配制：　特级矾石　粒度　５－３ｍｍ　１５－２０％；　特级矾石　粒度　３－１ｍｍ　２５－３０％ ；　特级矾石　粒度　１－０ｍｍ　１５－２０％；　特级矾石　粒度　＜０．０８８ｍｍ　５－１０％；　碳化硅　粒度　＜０．０４４ｍｍ　４－１０％；　熔融石英　粒度　１００目　１－５％；　氧化硅 微粉　１－５％；　高铝微粉　５μｍ　３－１０％；　煅烧氧化铝微粉　２μｍ　３－１０％；　特级焦宝石微粉　５μｍ　３－１０％；　纯铝酸钙水泥　Ａ７１　３－８％；　三聚磷酸钠　０．１－０．２％； 　其制作工艺是：先将三聚磷酸钠和纯铝酸钙水泥在混料机中预混合制成预混合料，再在混料机中将各粒度特级矾石、碳化硅、熔融石英、氧化硅微粉、高铝微粉、煅烧氧化铝微粉、特级焦宝石微粉和预混合料混合均匀，将混合好的浇注料分袋包装。...

【技术特征摘要】

【专利技术属性】
技术研发人员：陶贵华，范泳，郝瑞，
申请(专利权)人：北京通达耐火技术股份有限公司，
类型：发明
国别省市：11[中国|北京]