The invention relates to a preparation method of concave texture on the surface of plastic, which comprises: first, premixing the polymer, heat conduction assistant and defoamer evenly according to the proportion, then melting extrusion granulation to obtain plastic particles; finally, melting extrusion molding or injection molding plastic particles into plastic products, and finally carving concave texture. The invention can evenly heat the surface of plastic product under laser excitation by adding defoamer and heat conduction assistant, the polymer will not decompose, and the concave texture is formed by remelting and solidification, which has the characteristics of economy, environmental protection, automation, flexible change of texture pattern, etc.
【技术实现步骤摘要】
一种塑胶表面凹纹理的制备方法
本专利技术属于纹理成型方法
,特别涉及一种塑胶表面凹纹理的制备方法。
技术介绍
现实生活里人们大量使用塑胶产品,在塑胶产品表面进行各种图形和标记的纹理修饰,可以大大提高塑胶产品的视觉外观,吸引客户的眼球。皮纹在塑胶产品的美观中承担越来越重要的角色,但目前塑胶产品的纹理主要是依靠模具的皮纹来实现,通过塑胶粒子熔融挤出或者注塑,复制金属模具表面皮纹。金属模具表面皮纹是需要通过喷砂和化学刻蚀技术,加工周期长,皮纹形状唯一,价格昂贵,严重污染环境;且未经改性的塑胶粒子是无法采用激光雕刻纹理的。因此,需要开发一种针对塑胶粒子的新型纹理成型方法。
技术实现思路
本专利技术所要解决的技术问题是提供一种塑胶表面凹纹理的制备方法,该方法通过激光直接在塑胶产品表面雕刻凹纹理,不需要复制皮纹模具,经济、环保、可自动化、纹理形状可变,从而克服现有技术的不足。本专利技术提供了一种塑胶表面凹纹理的制备方法,包括:按重量份数,首先将聚合物100份、导热助剂0.1~1份和消泡剂5~10份按配比预混合均匀,然后熔融挤出造粒,得到塑胶粒子;将塑料粒子熔融挤出成型或注塑成型为塑胶产品,最后进行凹纹理雕刻,即可。所述聚合物为乙烯基类聚合物、苯基类聚合物、聚酯类聚合物的一种或几种。所述导热助剂为石墨、炭黑、钛黑、氧化铁黑、碳纳米管、石墨烯的一种或几种。所述导热助剂的导热系数≥1.2W/(m·K),其作用是让热量均匀传递分散,防止局部受激过热,导致基材树脂不稳定变化 ...
【技术保护点】
1.一种塑胶表面凹纹理的制备方法,包括:/n按重量份数,首先将聚合物100份、导热助剂0.1~1份和消泡剂5~10份按配比预混合均匀,然后熔融挤出造粒,得到塑胶粒子;将塑料粒子熔融挤出成型或注塑成型为塑胶产品,最后进行凹纹理雕刻,即可。/n
【技术特征摘要】
1.一种塑胶表面凹纹理的制备方法,包括:
按重量份数,首先将聚合物100份、导热助剂0.1~1份和消泡剂5~10份按配比预混合均匀,然后熔融挤出造粒,得到塑胶粒子;将塑料粒子熔融挤出成型或注塑成型为塑胶产品,最后进行凹纹理雕刻,即可。
2.根据权利要求1所述的制备方法,其特征在于:所述聚合物为乙烯基类聚合物、苯基类聚合物、聚酯类聚合物的一种或几种。
3.根据权利要求1所述的制备方法,其特征在于:所述导热助剂为石墨、炭黑、钛黑、氧化铁黑、碳纳米管、石墨烯的一种或几种。
4.根据权利要求1或...