The invention relates to a preparation method of a light high strength humidity regulating material, which belongs to the technical field of the preparation of functional indoor facing materials of buildings. First, the perlite shall be crushed, sieved through 100 mesh and dried; then the perlite and calcium hydroxide shall be measured with the calcium silicon ratio of 0.1-0.7, then the perlite and calcium hydroxide shall be measured with the calcium chloride ratio of 90% - 100%: 0% - 10%, and finally the water of 10% - 50% of the total weight shall be measured; after grinding and mixing all the above raw materials, they shall be pressed into massive samples under the molding pressure of 10-30mpa and demoulded Under the condition of 100 \u2103 ~ 220 \u2103, the product was cured by hydrothermal method for 1 ~ 24h, and then dried to be a lightweight and high-strength moisture regulating material. The process of the invention is simple, and the product density obtained is less than 1G / cm
【技术实现步骤摘要】
一种轻质高强度调湿材料的制备方法
本专利技术涉及一种轻质高强度调湿材料的制备方法，属于建筑物室内功能性饰面材料制备
技术介绍
珍珠岩是一种火山喷发的酸性熔岩，经急剧冷却而成的玻璃质岩石，因其具有珍珠裂隙结构而得名。珍珠岩主要由酸性火山玻璃组成，95％为玻璃相，65％～75％为无定形石英。珍珠岩在我国储量丰富，据统计，截止2015年底全国已探明珍珠岩矿43处，查明资源储量3.9×108t左右，其中河南省资源储量最大，约占全国总资源量的26％，其他省区如山西、内蒙古储量均超过千万吨。此外，珍珠岩具有优越的性质，其性脆、质轻，在加热条件下能迅速膨胀，具有隔音、隔热、耐高温、吸附性强、容量小、化学性质稳定、耐酸碱等特点，因此用途广泛。目前我国膨胀珍珠岩是国内使用最广泛的一类轻质保温材料。据有关部门统计，目前我国膨胀珍珠岩在市场上的应用比例为：建筑工程约60％、热管道保温约30％、装饰材料约10％。目前，膨胀珍珠岩在建筑工业上，主要是利用它容重轻、隔音、绝热的特点，大量用作混凝土和灰浆的骨料。一般珍珠岩混凝土...
【技术保护点】
1.一种轻质高强度调湿材料的制备方法，其特征是：/n先将珍珠岩粉碎，过100目筛并烘干，再以质量百分比量取珍珠岩：氢氧化钙＝92％～60％：8％～40％，接着，再量取珍珠岩和氢氧化钙：氯化钙＝90％～100％：0～10％，最后量取珍珠岩和氢氧化钙和氯化钙总重量的10％～50％的水；将上述量取的各原料研磨、混合均匀后，在10～30MPa的成型压力下压制成块状样品并脱模，在100℃～220℃条件下，进行水热固化1～24h，最后，经过烘干后制得块状固化产品为轻质高强度调湿材料；/n上述珍珠岩和氢氧化钙的具体计量以满足氢氧化钙中与珍珠岩混合物中的钙和硅的摩尔比达到钙硅比＝0.1～0...
【技术特征摘要】
1.一种轻质高强度调湿材料的制备方法，其特征是：
先将珍珠岩粉碎，过100目筛并烘干，再以质量百分比量取珍珠岩：氢氧化钙＝92％～60％：8％～40％，接着，再量取珍珠岩和氢氧化钙：氯化钙＝90％～100％：0～10％，最后量取珍珠岩和氢氧化钙和氯化钙总重量的10％～50％的水；将上述量取的各原料研磨、混...