The invention discloses polymer waterproof material for building, comprising the following components: polymer modified elastic emulsion, polyvinyl acetate calcium carbonate composite material, polyurethane, compound emulsifier, organic phosphate, liquid silica sol, Portland cement, micro silicon, fly ash, nanometer tin oxide antimony and nanometer titanium dioxide. The invention forms a multi-layer, non-destructive, permanent waterproof and anti-corrosion whole in the building and the base surface, and better displays the excellent characteristics of waterproof materials, such as cold resistance, heat resistance, aging resistance, antibacterial, environmental protection, long service life, etc.
【技术实现步骤摘要】
建筑用聚合物防水材料
本专利技术涉及一种防水材料,具体涉及建筑用聚合物防水材料。
技术介绍
目前,全世界用于建筑物防水的材料概括起来无非有两中:一种是刚性防水;一种是柔性防水。其中普遍采用的刚性防水是在建筑物基面另加钢筋混凝土砂浆防水层。这种防水层与基面结合不够紧密,且防水层本身存在分子空隙,在水的作用下钢筋容易腐蚀膨胀,导致防水层开裂而失去防水防腐效果。同样,目前普遍采用的柔性防水是在建筑物基面涂刷有机物防水涂料,形成防护层。这种防护层不但容易老化、分层、脱落,也容易在外力的作用下被破坏,从而失去应有的防水防腐性能。上述两种防水材料都是在建筑物表面涂刷防水层。这样,无论是刚性防水还是柔性防水,都不能与建筑物基面结合为统一的整体。因此,很容易出现分层、开裂、老化、脱落等现象,严重影响了防水的质量和效果,无法对建筑物真正起到防水防腐的性能,从而降低了建筑物的使用寿命。
技术实现思路
本专利技术所要解决的技术问题是现有防水材料防水效果差,使用寿命短,目的在于提供建筑用聚合物防水材料,解决现有防水材料防水效果差,使用寿命短的问题。本专利技术通过下述技术方案实现:建筑用聚合物防水材料,包括以下组分:聚合物改性弹性乳液、聚醋酸乙烯酯碳酸钙复合材料、聚氨酯、复合乳化剂、有机磷酸盐、液态硅溶胶、硅酸盐水泥、微硅、粉煤灰、纳米氧化锡锑、纳米钛白粉。本专利技术在建筑物及基面形成多层次的、不易破坏的永久性防水防腐整体,更好的发挥防水材料耐寒、耐热、耐老化、抗菌、环保、寿命长等的优良特性 ...
【技术保护点】
1.建筑用聚合物防水材料,其特征在于,包括以下组分:聚合物改性弹性乳液、聚醋酸乙烯酯碳酸钙复合材料、聚氨酯、复合乳化剂、有机磷酸盐、液态硅溶胶、硅酸盐水泥、微硅、粉煤灰、纳米氧化锡锑、纳米钛白粉。/n
【技术特征摘要】
1.建筑用聚合物防水材料,其特征在于,包括以下组分:聚合物改性弹性乳液、聚醋酸乙烯酯碳酸钙复合材料、聚氨酯、复合乳化剂、有机磷酸盐、液态硅溶胶、硅酸盐水泥、微硅、粉煤灰、纳米氧化锡锑、纳米钛白粉。
2.根据权利要求1所述的建筑用聚合物防水材料,其特征在于,包括以下重量份数的组分:20-30份聚合物改性弹性乳液、10-30份聚醋酸乙烯酯碳酸钙复合材料、10-20份聚氨酯、10-15份复合乳化剂、8-12份有机磷酸盐、5-10份液态硅溶胶、8-20份硅酸盐水泥、10-30份微硅、20-25份粉煤灰、3-8份纳米氧化锡锑、3-8份纳米钛白粉。
3.根据权利要求2所述的建筑用聚合物防水材料,其特征在于,包括以下重量份数的组分:25-30份聚合物改性...