A coating method for TFT-LCD substrate glass, including TFT-LCD glass substrate, is characterized by the following steps: 1. Float forming TFT-LCD substrate glass; 2. Spraying coating solution on both sides of the substrate glass, controlling glass movement speed 10 15 m/min, UV curing brightness 500_1000 mj/cm_, curing machine 1050 *100W 1300V 3A side by side, 4 rows of 365 nm, coating thickness 6_um TFT 3. CD glass substrates were sprayed with 1 5% NaOH and 70 80 C circulating water for 5 10 s before use to remove the coating, and the film slag was filtered through filters and cleaned manually. The invention has the advantages of: 1. improving the yield of production line and production efficiency; 2. replacing spacer paper and reducing packaging cost; 3. reducing glass scratches and ADG production.
【技术实现步骤摘要】
一种TFT-LCD基板玻璃的镀膜方法
本专利技术属玻璃制备领域，涉及TFT-LCD玻璃制备领域，具体涉及一种TFT-LCD基板玻璃的镀膜方法。
技术介绍
TFT-LCD基板玻璃制作过程中需要对四边进行切割、研磨，在切割四边的过程中会产生一定量的玻璃粉尘，玻璃粉尘落在玻璃基板表面，极易造成玻璃表面的划伤。目前生产中TFT-LCD玻璃基板表面多用间隔纸进行保护，因间隔纸受潮、粘连极易造成玻璃表面产生划伤、污渍。
技术实现思路
本专利技术的目的是为了有效防止异物、划伤、污渍、减少ADG（热黏附）对玻璃基板造成的划伤、保护玻璃面，提供了一种TFT-LCD基板玻璃的镀膜方法。一种TFT-LCD基板玻璃的镀膜方法，包括现有浮法生产的TFT-LCD玻璃基板，其特征在于：在TFT-LCD玻璃基板两面涂覆一层6-8µm镀膜液，包括以下步骤：1.选用如下重量份数比的玻璃配合料：SiO258～63%、B2O38～11%、Al2O314～18%、CaO3～8%、MgO0～4%、SnO0~1%、ZnO0～10%，经浮法成型制得的TFT-LCD基板玻璃，对TFT-LCD基板玻璃进行检查，使得玻璃...
【技术保护点】
1.一种TFT‑LCD基板玻璃的镀膜方法，包括现有浮法生产的TFT‑LCD玻璃基板，其特征在于：在TFT‑LCD玻璃基板两面涂覆一层6‑8µm 镀膜液，包括以下步骤：1）.选用如下重量份数比的玻璃配合料：SiO2 58～63%、B2O3 8～11%、Al2O3 14～18%、CaO 3～8%、MgO 0～4%、SnO 0~1%、ZnO 0～10%，经浮法成型制得的TFT‑LCD基板玻璃，对TFT‑LCD基板玻璃进行检查；2）.采用喷雾设备对TFT‑LCD基板玻璃的两面喷涂镀膜液，镀膜液为韩国玉金化学生产的镀膜液，控制TFT‑LCD基板玻璃移动的速度为10‑15 m/min，...
【技术特征摘要】
1.一种TFT-LCD基板玻璃的镀膜方法，包括现有浮法生产的TFT-LCD玻璃基板，其特征在于：在TFT-LCD玻璃基板两面涂覆一层6-8µm镀膜液，包括以下步骤：1）.选用如下重量份数比的玻璃配合料：SiO258～63%、B2O38～11%、Al2O314～18%、CaO3～8%、MgO0～4%、SnO0~1%、ZnO0～10%，经浮法成型制得的TFT-LCD基板玻璃，对TFT-LCD基板玻璃进行检查；2）.采用喷雾设备对TFT-LCD基板玻璃的两面喷涂镀膜液，镀膜液为韩国...