The invention provides a method for preparing silicon-vanadium nitride, which relates to the field of alloy smelting technology. The method has the advantages of low raw material cost, simple process route, short production time and low requirement for equipment, and can obtain silicon-vanadium nitride products with higher nitrogen content and better alloying effect. The steps of the method include: S1, mixing vanadium source, silicon source and carbon powder for use; S2, in nitrogen atmosphere, right. The mixture obtained from S1 is roasted to obtain silicon vanadium nitride. The technical scheme provided by the invention is suitable for the preparation process of silicon vanadium nitride.
【技术实现步骤摘要】
一种制备氮化硅钒的方法
本专利技术涉及合金冶炼
，尤其涉及一种制备氮化硅钒的方法。
技术介绍
在含钒微合金钢中，氮是一种有益的元素，钒对钢的强化作用是通过形成钒的碳氮化物实现的，钢中增氮可以促进钒的析出，析出的钒氮化物可以抑制晶粒长大，具有析出强化和细晶强化的作用。能提升钢的强度和韧性，优化钢的性能。与添加钒铁相比，添加氮钒合金能节省大量的钒的用量，降低合金化成本。钢材增氮常用的方法有出钢时向钢液中添加氮化物，其中氮化硅中氮的理论质量百分数是40％，相较于氮化钒的理论质量百分数21％，能提供更加充足的氮元素。硅在特定钢种中较为常见，作为合金元素，硅对钢的性能有提升作用，能减少晶体的各向异性倾向，使磁化容易，提高铁素体的磁导率，提高磁感强度。氮化硅的生产方法包括硅粉直接氮化法，二氧化硅还原氮化法，液相法，气相法等，其中与本专利技术相关的有二氧化硅还原氮化法。氮化钒的生产方法中主要有美国专利US4040814、中国专利CN1422800A以及中国专利CN1644510的方法。其中中国专利CN1644510公开了一种工业微波炉加热生产氮化钒的方法，该方法以...
【技术保护点】
1.一种制备氮化硅钒的方法，其特征在于，步骤包括：S1、将钒源、硅源和碳粉混匀做压块处理后待用；S2、在氮气气氛下，对S1获得的混合物料进行焙烧，得到氮化硅钒。
【技术特征摘要】
1.一种制备氮化硅钒的方法，其特征在于，步骤包括：S1、将钒源、硅源和碳粉混匀做压块处理后待用；S2、在氮气气氛下，对S1获得的混合物料进行焙烧，得到氮化硅钒。2.根据权利要求1所述的制备氮化硅钒的方法，其特征在于，所述钒源为五氧化二钒和三氧化二钒中的一种或两者的混合。3.根据权利要求1所述的制备氮化硅钒的方法，其特征在于，所述硅源为二氧化硅。4.根据权利要求1所述的制备氮化硅钒的方法，其特征在于，所述碳粉为碳黑和石墨中的一种或两者的混合。5.根据权利要求1所述的制备氮化硅钒的方法，其特征在于，所述焙烧的具体条件是：反应温度为10...
【专利技术属性】
技术研发人员：张国华，周英聪，徐瑞，
申请(专利权)人：北京科技大学，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。