The invention relates to a method for preparing grinding head materials, abrasives and abrasives. The grinding head materials include the following components: 1 3 parts of diamond powder, 3 5 parts of metal powder, 3 5 parts of binder, 3 5 parts of ceramic powder and 0.5 parts of trace elements. It can be made into grinding head of abrasive tools. Diamond, metal powder and ceramic powder are components with high hardness. The components are bonded by binder. Through isostatic pressing, baking, drying and high temperature sintering, diamond, metal powder, ceramic powder and trace elements are bonded tightly. It has good hardness and wear resistance. It is suitable for grinding glass products. It is not easy to drop particles and has long service life.
【技术实现步骤摘要】
磨头材料、磨具及磨具的制备方法
本专利技术涉及磨具及其制备工艺
，特别是涉及磨头材料、磨具及磨具的制备方法。
技术介绍
目前国内外用的磨头，基本都是电镀的，将金属电镀于磨头的表面，形成金属层，作为磨削层。但是随着技术的发展，玻璃材料的成份升级。电镀磨头在使用过程中，容易掉颗粒，不耐磨，使用寿命短，导致产品出现外观不良和尺寸不稳定等问题，越来越难以满足用户需求。
技术实现思路
基于此，有必要针对上述问题，提供一种磨头材料，可制成粘结紧密，硬度佳、耐磨的磨头，使用过程中不易掉粉，可长期使用。一种磨头材料，包括以下重量份的组分：金刚石粉1份-3份、金属粉3份-5份、粘结剂3份-5份、陶瓷粉3份-5份及微量元素0.5份-1份。上述磨头材料，可制成磨具的磨头，金刚石、金属粉及陶瓷粉均为硬度较高的成分，通过粘结剂将各组分粘合，通过等静压成型、烘烤干燥及高温烧结等工序，金刚石、金属粉、陶瓷粉及微量元素紧密粘合，硬度及耐磨性佳，适用于磨削玻璃制品，不容易掉颗粒，使用寿命长。在其中一个实施例中，金属粉选自铬、钼、钨、钛中的一种或几种。在其中一个实施例中，粘结剂为酚醛树脂。在其中一...
【技术保护点】
1.一种磨头材料，其特征在于，包括以下重量份的组分：金刚石粉1份‑3份、金属粉3份‑5份、粘结剂3份‑5份、陶瓷粉3份‑5份及微量元素0.5份‑1份。
【技术特征摘要】
1.一种磨头材料，其特征在于，包括以下重量份的组分：金刚石粉1份-3份、金属粉3份-5份、粘结剂3份-5份、陶瓷粉3份-5份及微量元素0.5份-1份。2.根据权利要求1所述的磨头材料，其特征在于，所述金属粉选自铬、钼、钨、钛中的一种或几种。3.根据权利要求1所述的磨头材料，其特征在于，所述粘结剂为酚醛树脂。4.根据权利要求1所述的磨头材料，其特征在于，所述陶瓷粉为氮化硅陶瓷粉；所述陶瓷粉中氮化硅的质量百分含量为10％-50％。5.根据权利要求1所述的磨头材料，其特征在于，所述微量元素包括铼和钽。6.一种磨具，其特征在于，包括磨头，所述磨头采用权利要求1至5任一项所述的磨头材料制...