The invention relates to a CBN resin bonded abrasive tool and a preparation method thereof, belonging to the technical field of abrasive abrasives. The CBN resin bond abrasive tool of the invention is made of the following raw materials with mass percentage: thermosetting resin 10-20%, cubic boron nitride 10-25%, metal powder 20-40%, silicon carbide 5-15%, calcium sulfate 3-10%, solid lubricant 5-10%. The CBN resin bond abrasive tool of the invention makes use of the high fluidity of the thermosetting resin in the curing stage to infiltrate metal powder, silicon carbide and calcium sulfate evenly and well to improve the bonding strength, and greatly enhances the strength, heat dissipation, grinding efficiency and self-sharpening of the CBN resin bond abrasive tool by adding calcium sulfate, metal powder, silicon carbide and solid lubricant. The uniformity of abrasive structure is improved.
【技术实现步骤摘要】
一种CBN树脂结合剂磨具及其制备方法
本专利技术涉及一种CBN树脂结合剂磨具及其制备方法，属于磨料磨具
技术介绍
树脂砂轮作为砂轮中重要的一类，按磨料的不同分为普通树脂砂轮和超硬树脂砂轮，普通树脂砂轮是以白刚玉、棕刚玉、碳化硅等普通磨料为主要磨削成分的砂轮，超硬砂轮是以金刚石或CBN为主要磨削成分的砂轮。其中，树脂CBN砂轮以其较强的耐磨性、抗压性以及较高的硬度和良好的自锐性，广泛用于粗磨、荒磨、切断和自由磨削，如磨钢锭，铸件打毛刺等。现有技术中，授权公告号为CN103639908B的中国专利技术专利中公开了一种超硬CBN磨具，该超硬CBN磨具包括砂轮磨料层；砂轮磨料层是由以下重量份数的原料制成的：树脂50～55份，铜粉5～10份，固体润滑剂5～8份，六钛酸钾晶须10～15份，CBN磨料25～30份；所述固体润滑剂由二硫化钼和石墨组成。该CBN砂轮具有使用寿命长、磨损少、尺寸稳定等优点，但由于砂轮磨料层中树脂含量较多，粉状颗粒太少，易导致磨具的自锐性差，进而导致磨削效率低、散热性差、工件表面质量及形位精度差等连锁性问题。
技术实现思路
本专利技术的目的是提供...
【技术保护点】
1.一种CBN树脂结合剂磨具，其特征在于：由以下质量百分比的原料制成：热固性树脂10～20％、立方氮化硼10～25％，金属粉20～40％、碳化硅5～15％、硫酸钙3～10％、固体润滑剂5～10％。
【技术特征摘要】
1.一种CBN树脂结合剂磨具，其特征在于：由以下质量百分比的原料制成：热固性树脂10～20％、立方氮化硼10～25％，金属粉20～40％、碳化硅5～15％、硫酸钙3～10％、固体润滑剂5～10％。2.根据权利要求1所述的CBN树脂结合剂磨具，其特征在于：所述热固性树脂为高流动性热固性树脂。3.根据权利要求1所述的CBN树脂结合剂磨具，其特征在于：所述硫酸钙为硫酸钙晶须。4.根据权利要求3所述的CBN树脂结合剂磨具，其特征在于：所述硫酸钙晶须的平均长度为所述立方氮化硼的平均粒径的1/3～1/2...
【专利技术属性】
技术研发人员：史林峰，刘权威，赵延军，
申请(专利权)人：郑州磨料磨具磨削研究所有限公司，
类型：发明
国别省市：河南,41