一种高弹性橡胶制品制造技术

本发明专利技术涉及一种高弹性橡胶制品，主要由以质量份数计的以下成分组成：四丙氟橡胶40‑80份、硅橡胶40‑120份、环氧大豆油3‑5份、聚酰胺0.5‑0.6份、松焦油1‑4份、聚酰亚胺树脂0.5‑0.8份、硫化剂0.3‑0.8份、补强剂0.05‑0.4份、沥青2‑4份、氧化镁0.5‑1.2份、氧化锌0.05‑0.4份、氯化石蜡0.05‑0.1份、玻璃纤维5‑30份、改性蛭石粉0.1‑0.4份。本发明专利技术的弹性极佳，厚度弹性比高，且在不损失强度的前提下还减轻了制品的密度。

A High Elasticity Rubber Product

The invention relates to a high elasticity rubber product, which is mainly composed of 40 80 copies of tetrapropylfluororubber, 40 120 copies of silicone rubber, 3 5 copies of epoxy soybean oil, 0.5 0.6 copies of polyamide, 1 4 copies of pine tar, 0.5 0.8 copies of polyimide resin, 0.3 0.8 copies of vulcanizing agent, 0.05 0.4 copies of reinforcing agent, 2 4 copies of asphalt, 0.5 1.2 copies of magnesium oxide and zinc oxide. 0.05 0.4 phr, chlorinated paraffin 0.05 0.1 phr, glass fiber 5 30 phr, modified vermiculite powder 0.1 0.4 phr. The invention has excellent elasticity, high thickness elasticity ratio, and reduces the density of products without losing strength.

【技术实现步骤摘要】
一种高弹性橡胶制品
本专利技术涉及高分子材料
，尤其涉及一种高弹性橡胶制品。
技术介绍
橡胶行业是国民经济的重要基础产业之一。它不仅为人们提供日常生活不可或缺的日用、医用等轻工橡胶产品，而且向采掘、交通、建筑、机械、电子等重工业和新兴产业提供各种橡胶制生产设备或橡胶部件。可见，橡胶行业的产品种类繁多，后向产业十分广阔。橡胶的弹性直接影响其减震性能，以橡胶作为阻尼结构的领域中需要超高的弹性。
技术实现思路
为了解决上述技术问题，提供一种弹性高、密度低的橡胶制品，本专利技术提供以下技术方案：一种高弹性橡胶制品，由以质量份数计的以下成分组成：四丙氟橡胶40-80份、硅橡胶40-120份、环氧大豆油3-5份、聚酰胺0.5-0.6份、松焦油1-4份、聚酰亚胺树脂0.5-0.8份、硫化剂0.3-0.8份、补强剂0.05-0.4份、沥青2-4份、氧化镁0.5-1.2份、氧化锌0.05-0.4份、氯化石蜡0.05-0.1份、玻璃纤维5-30份、改性蛭石粉0.1-0.4份。进一步的，还包括有机硅0.5-2.5份。进一步的，还包括硬脂酸2-4份。进一步的，还包括松焦油0.2-1.5份。本专利技术的弹性本文档来自技高网...

【技术保护点】
1.一种高弹性橡胶制品，其特征在于：由以质量份数计的以下成分组成：四丙氟橡胶40‑80份、硅橡胶40‑120份、环氧大豆油3‑5份、聚酰胺0.5‑0.6份、松焦油1‑4份、聚酰亚胺树脂0.5‑0.8份、硫化剂0.3‑0.8份、补强剂0.05‑0.4份、沥青2‑4份、氧化镁0.5‑1.2份、氧化锌0.05‑0.4份、氯化石蜡0.05‑0.1份、玻璃纤维5‑30份、改性蛭石粉0.1‑0.4份。

【技术特征摘要】
1.一种高弹性橡胶制品，其特征在于：由以质量份数计的以下成分组成：四丙氟橡胶40-80份、硅橡胶40-120份、环氧大豆油3-5份、聚酰胺0.5-0.6份、松焦油1-4份、聚酰亚胺树脂0.5-0.8份、硫化剂0.3-0.8份、补强剂0.05-0.4份、沥青2-4份、氧化镁0.5-1.2份、氧化锌0.05-0.4份、氯...