The invention discloses a preparation method of submicron potassium nitrate fiber, which takes potassium nitrate and nano-silica as raw materials and obtains submicron potassium nitrate fiber crystal by simple low temperature solvent evaporation crystallization method. The preparation method of the present invention has the advantages of low operation cost, simple operation and low technical requirements. High purity and small particle size sub-micron potassium nitrate crystals are prepared by controlling the concentration of potassium nitrate solution, the content of nanoparticles, the dispersion degree of nanoparticles and the ambient temperature in the crystallization process, and the obtained crystals are bright in color and have a slender fiber with a diameter between 0.4 and 2 microns. It is not easy to agglomerate and shows obvious advantages.
【技术实现步骤摘要】
亚微米硝酸钾纤维的制备方法
本专利技术涉及一种硝酸钾的制备方法，特别是一种亚微米硝酸钾纤维的制备方法。
技术介绍
硝酸钾是一种重要的工农业原料，在国民经济建设中占有至关重要的地位。同时，硝酸钾由于含氧量高、顿感、化学性能稳定等优良性能也常常被用于含能材料中。通常硝酸钾作为含能材料的氧化剂广泛用于烟火药剂、汽车安全气囊点火药、混合炸药、固体推进剂等方面。为了提高各种点火药、烟火剂性能，学者们提出了许多方法。如：氧化剂的含量及配比的改变、氧化剂粒径的改变、燃烧剂含量及配比的改变和添加金属纤维等。其中国内外大量学者研究了氧化剂的粒度及其分布对点火药和烟火剂性能的影响。结果表明，氧化剂粒度对点火药的燃速、热分解性能以及机械性能有很大的影响。为此许多学者将氧化剂进行超细化，发现点火药的性能有了很大的提升。由此可知，减小氧化剂的平均粒度，能够提高点火药的燃烧和爆炸性能以及推进剂的燃速。因此硝酸钾的细化在提高点火药的性能研究中有重要意义。对于含能材料的细化，科研工作者已经报道了多种的制备方法。其中包括溶胶-凝胶法、溶剂-非溶剂法、超临界流体法、微乳液法、机械球磨法、气流粉碎法、...
【技术保护点】
1.亚微米硝酸钾纤维的制备方法，其特征在于：包括如下步骤：在硝酸钾溶液中加入微量纳米二氧化硅颗粒，在细胞粉碎机中进行超声处理，形成硝酸钾基纳米流体，再在低于室温的环境中，倒入玻璃培养皿中进行结晶培养，真空干燥后得到所述的亚微米硝酸钾纤维，其中，硝酸钾溶液浓度低于0.01 mol/L，SiO2/KNO3质量比介于5%‑20%。
【技术特征摘要】
1.亚微米硝酸钾纤维的制备方法，其特征在于：包括如下步骤：在硝酸钾溶液中加入微量纳米二氧化硅颗粒，在细胞粉碎机中进行超声处理，形成硝酸钾基纳米流体，再在低于室温的环境中，倒入玻璃培养皿中进行结晶培养，真空干燥后得到所述的亚微米硝酸钾纤维，其中，硝酸钾溶液浓度低于0.01mol/L，SiO2/KNO3质量比介于5%-20%。2.如权利要求1所述的制...
【专利技术属性】
技术研发人员：何思，陈迁乔，车海山，颜海龙，漆中路，
申请(专利权)人：南京理工大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。