The present invention relates to a NO oxidation catalyst based on selective catalytic reduction technology and its preparation method. The catalyst uses cordierite honeycomb ceramics as catalyst carrier. First, the coating slurry containing precious metal platinum is coated on the surface of the catalyst carrier. After drying and roasting, a certain amount of precious metal Pd solution is immobilized at one end of the catalyst by impregnation method, and the impregnated precious metal Pd is immersed. The amount of solution is 1/3 of the total water absorption of the catalyst. The coating slurry is prepared by using molecular sieve as HC adsorbent, SiO 2 as dispersant, zirconium acetate as heat stabilizer, precious metal platinum as active component and adding aluminium binder. The process steps of the invention are simple. The prepared catalyst is impregnated with precious metal platinum or Pd in the direction of air intake. The improved catalyst can increase the oxidation rate of NO at low temperature, widen the temperature window between 40% and 70%, and improve the stability of the catalyst.
【技术实现步骤摘要】
一种基于选择性催化还原技术的NO氧化催化剂及其制备方法
本专利技术涉及一种基于选择性催化还原技术的NO氧化催化剂及其制备方法，属于柴油车氧化性催化剂的制备
技术介绍
汽车尾气污染已成为大气污染的主要来源之一。城市中大部分的NOx、CO、HC和PM都是由汽车尾气产生的。NOx、CO、HC、PM不但对人体造成损伤而且在一定的条件下产生蓝色的光化学烟雾，使植被死亡，人类生存的环境遭到破坏。现排放法规定，北京、上海将会实施柴油车国五排放标准，柴油车国四排放标准的全国实施日期将近，因此，对柴油车氧化性催化剂的催化转化效率也提出了更高的要求。柴油车氧化性催化剂(DOC)用于氧化柴油车的尾气中CO、NO、HC及PM中的可溶有机成分(SOF)，其涂层主要由氧化物涂层和活性贵金属组分组成，贵金属是氧化性催化剂的关键组分，对于柴油车DOC而言，就是利用DOC能降低柴油机尾气中的HC、CO和SOF等的化学反应的活化能，使这些物质能与尾气中的氧气在较低的温度下进行氧化反应，转化为CO2和H2O；氧化催化剂通常以蜂窝陶瓷或者蜂窝金属为载体，其上负载氧化物涂层和活性金属组分，常用的...
【技术保护点】
1.一种基于选择性催化还原技术的NO氧化催化剂，其特征在于：催化剂以堇青石蜂窝陶瓷为催化剂载体，催化剂载体的表面涂覆含贵金属铂的涂层浆液，催化剂的一端采用浸渍法固定有一定量的贵金属Pd溶液，所述固定的贵金属Pd溶液量为所述催化剂总吸水量的1/3，所述涂层浆液采用分子筛为HC吸附材料，SiO2为分散剂，乙酸锆为热稳定助剂，贵金属铂为活性组分，加入铝胶粘结剂制成。
【技术特征摘要】
1.一种基于选择性催化还原技术的NO氧化催化剂，其特征在于：催化剂以堇青石蜂窝陶瓷为催化剂载体，催化剂载体的表面涂覆含贵金属铂的涂层浆液，催化剂的一端采用浸渍法固定有一定量的贵金属...