The invention discloses a sizing agent for polyolefin resin-based carbon fiber suspension and a preparation method thereof. The sizing agent of polyolefin resin-based carbon fiber suspension is composed of polyolefin resin powder, sodium polyacrylate, aliphatic alcohol polyoxyethylene ether and deionized water. The total mass of solid component is 100%. Among them, polyolefin resin powder is 65-75wt%, sodium polyacrylate is 10-15wt%, aliphatic alcohol polyoxyether is 15-20wt%. The sizing agent of the invention is used for preparing carbon fibers, and the sizing carbon fibers prepared are suitable for carbon fibre fabrics, preprepregs and other intermediates for polyolefin resin matrix composites, and have good processing performance and interfacial bonding ability.
【技术实现步骤摘要】
一种聚烯烃树脂基碳纤维悬浮液上浆剂及其制备方法
本专利技术属于碳纤维上浆剂
，特别涉及一种聚烯烃树脂基碳纤维悬浮液型上浆剂及其制备方法。
技术介绍
碳纤维增强热塑性复合材料是近年来快速发展的一种增强材料，在其制备过程中，碳纤维首先被切断成5-20mm长度的短纤维，然后与热塑性树脂进行混配，进一步通过挤出注塑等工艺制备成连续均相体系的复材型材。聚烯烃树脂原料丰富，价格低廉，容易加工成型，综合性能优良，是目前应用最为广泛的热塑性树脂。碳纤维增强聚烯烃树脂基复合材料具有良好的经济性、可加工性和可循环性，目前逐渐受到业界重视。碳纤维经过系列高温处理，表面呈相对惰性，纤维整体松散。因此，需要在碳纤维表面涂覆一层上浆剂对碳纤维进行保护，改善碳纤维丝束的集束性和界面性能。目前工业用上浆剂多为环氧树脂型，其在高温或长时间储存条件下容易老化变硬，导致上浆碳纤维丝束僵硬、加工和界面性能下降。因此，在制备聚烯烃树脂基复材时，适宜采用聚烯烃树脂类上浆剂对碳纤维进行表面处理。由于具有同样的结构组成和工艺性能，基体树脂可以均匀深入地浸渍碳纤维内部，加工难度大幅降低；同时孔洞缺陷减少，复...
【技术保护点】
1.一种聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于：其由聚烯烃树脂粉末、聚丙烯酸钠、脂肪醇聚氧乙烯醚和去离子水组成；以固体组分的总质量为100％计，其中：聚烯烃树脂粉末 65～75wt％聚丙烯酸钠 10～15wt％脂肪醇聚氧乙烯醚 15～20wt％。
【技术特征摘要】
1.一种聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于：其由聚烯烃树脂粉末、聚丙烯酸钠、脂肪醇聚氧乙烯醚和去离子水组成；以固体组分的总质量为100％计，其中：聚烯烃树脂粉末65～75wt％聚丙烯酸钠10～15wt％脂肪醇聚氧乙烯醚15～20wt％。2.根据权利要求1所述的聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于：所述的聚烯烃树脂粉末是包括但不限于聚乙烯、聚丙烯、聚丁烯或聚异丁烯的通用聚烯烃树脂。3.根据权利要求1所述的聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于：所述的聚烯烃树脂粉末的数均分子量在1.0万～4.0万之间。4.根据权利要求1所述的聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于：所述的聚烯烃树脂粉末平均直径在10～60微米之间。5.根据权利要求1所述的聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于，所述的聚丙烯酸钠的数均分子量在1000～5000之间。6.根据权利要求1所述的聚烯烃树脂基碳纤维悬浮液上浆剂，其特征在于：脂肪醇聚氧乙烯...
【专利技术属性】
技术研发人员：季春晓，黄翔宇，曹阿民，刘瑞超，刘杰，王平，许璐璐，黄猛，
申请(专利权)人：中国石油化工股份有限公司，中国石化上海石油化工股份有限公司，
类型：发明
国别省市：北京,11