The present invention relates to an aluminized ternary copolymer polypropylene tape casting film resin composition, which consists of 1000 copolymer polypropylene resins, 1:1.0-1.6 copies of antioxidant, 2:0.5-1.0 copies of antioxidant, 0.15-0.5 copies of halogen absorbent, and the ternary copolymer polypropylene resin is composed of 5.5-10wt% 1_butene by weight percentage. 0.5-1.5wt% ethylene and propylene are the rest. The ternary copolymer polypropylene resin composition of the invention can satisfy the processing performance, aluminizing performance, optical performance and thermal bonding performance of food-grade aluminized film, and also has excellent impact strength, rigidity and low n-hexane extract, which fully meets the production requirements of high-end tape packaging manufacturers for aluminized tape film.
【技术实现步骤摘要】
镀铝三元共聚聚丙烯流延膜树脂组合物
本专利技术属于高分子材料聚丙烯树脂
，具体涉及一种专用于制造镀铝聚丙烯流延膜的聚丙烯树脂组合物。
技术介绍
镀铝聚丙烯流延膜(Metalizecastpolypropylene；MCPP)是塑胶工业中通过流延挤塑工艺并经真空镀铝制成的一种聚丙烯薄膜。MCPP与LLDPE、LDPE、HDPE、PET等其他薄膜相比，成本更低，产量更高，比PE薄膜挺度更高，具有优良水气和异味阻隔性，能满足一般耐热、耐化学、耐磨、阻氧、阻湿等的使用要求，普遍用作食品包装等领域。近年来，随着国外MCPP专用料的不断开发，流延设备技术的飞速发展，应用领域的不断开拓，MCPP薄膜己成为塑料包装薄膜中发展趋势最快的薄膜之一，据估计未来几年MCPP市场需求量仍将保持10％以上的速度快速增长。作为食品包装用MCPP专用料，除了特定的理化性能外还要求较低的热封温度以提高产品的热封强度。现有技术通常采用三元共聚方法制造MCPP专用料，在聚合时引入2～3％的共聚单体1-丁烯和乙烯与丙烯共聚而成，通常乙烯含量高于1-丁烯，由于共聚单体的引入，降低了材料的结晶性能，熔...
【技术保护点】
1.一种镀铝三元共聚聚丙烯流延膜树脂组合物，由以下重量份的原料组成：
【技术特征摘要】
1.一种镀铝三元共聚聚丙烯流延膜树脂组合物，由以下重量份的原料组成：其中，所述的三元共聚聚丙烯树脂由以下重量百分比的组分组成：5.5～10wt％1-丁烯，0.5～1.5wt％乙烯，其余为丙烯。2.根据权利要求1所述的一种镀铝三元共聚聚丙烯流延膜树脂组合物，其特征在于：所述三元共聚聚丙烯树脂由以下重量百分比的组分组成：5.5～7wt％1-丁烯，1.2～1.5wt％乙烯，其余为丙烯。3.根据权利要求1所述的一种镀铝三元共聚聚丙烯流延膜树脂组合物，其特征在于：所述的抗氧剂1为酚类抗氧剂；抗氧剂2为亚磷酸酯类抗氧剂。4.根据权利要求3所述的一种镀铝三元共聚聚丙烯流延膜树脂组合物，其特征在于：所述的酚类抗氧剂为四[3-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊...
【专利技术属性】
技术研发人员：沈锋明，单国荣，王荣和，
申请(专利权)人：中国石油化工股份有限公司，中国石化上海石油化工股份有限公司，
类型：发明
国别省市：北京,11