The invention relates to the technical field of TPV material preparation, which is a flame-retardant TPV material. It consists of EPDM 20_40, PC 5_10, SEBS 5_10, PP 10_20, flame retardant 10_20, phenolic resin 1_3, paraffin 5_10, Color Masterbatch 1_3, calcium carbonate 5_10, EVA 1_3, and EPDM, PC, PP, paraffin, phenolic resin, phenolic resin and EVA 1_3 are added into the blend when preparing. After mixing for 15 to 20 minutes, the twin-screw extruder is added to dynamic vulcanization for 1 to 3 minutes at the internal temperature of 210 to 230 degrees Celsius, then SEBS, flame retardant and color masterbatch are added to mix for 1 to 3 minutes at 210 to 230 degrees Celsius, granulation, drying and packaging are obtained; the product of the invention has excellent mechanical properties, delicate handle and can be widely used outside various products. Surface decoration.
【技术实现步骤摘要】
一种阻燃TPV材料
本专利技术属于TPV材料制备
，具体是一种阻燃TPV材料。
技术介绍
目前，TPV材料因具有良好的低压缩变形性能、优良的耐酸碱性、优异的抗冲击性能及热塑性塑料易加工特性，被大量地应用在各种产品外表面装饰材料使用，但是也存在普通塑料易燃的缺点，限制了其大面积使用，因此，研发一种具有良好阻燃性的TPV材料，来拓展其应用范围，对TPV材料的发展是十分有必要的。
技术实现思路
本专利技术的目的就是针对目前TPV材料在用于外表面装饰材料使用时，由于其易燃的特性限制了其应用场合的问题，提供一种阻燃TPV材料。本专利技术的一种阻燃TPV材料，由下述重量份原料组成：EPDM20-40PC5-10SEBS5-10PP10-20阻燃剂10-20酚醛树脂1-3石蜡5-10色母粒1-3碳酸钙5-10EVA1-3；制备时，将EPDM、PC、PP、石蜡、酚醛树脂、碳酸钙、EVA加入混炼机内混炼15-20分钟，混炼完成后加入双螺杆挤出机内在温度为210-230℃条件下动态硫化1-3分钟，然后加入SEBS、阻燃剂、色母粒混合后在温度为210-230℃下混合1-3分钟，切粒、...
【技术保护点】
1.一种阻燃TPV材料，其特征在于由下述重量份原料组成：EPDM 20‑40 PC 5‑10SEBS 5‑10 PP 10‑20阻燃剂 10‑20 酚醛树脂 1‑3石蜡 5‑10 色母粒 1‑3碳酸钙 5‑10 EVA 1‑3；制备时，将EPD...
【技术特征摘要】
1.一种阻燃TPV材料，其特征在于由下述重量份原料组成：EPDM20-40PC5-10SEBS5-10PP10-20阻燃剂10-20酚醛树脂1-3石蜡5-10色母粒1-3碳酸钙5-10EVA1-3；制备时，将EPDM、PC、PP、石蜡、酚醛树脂、碳酸钙、EVA加入混炼机内混炼15-20分钟，混炼完成后加入双螺杆挤出机...
【专利技术属性】
技术研发人员：徐逢来，
申请(专利权)人：湖北恒标塑胶有限公司，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。