The invention relates to the technical field of preparing PVC cable material, which is a kind of PVC material for improving flexibility. It consists of the following raw materials: PVC 50 65, CPE 3 8, PE 3 8, TPV 5 10, soybean oil 1 3, trioctyl phthalate 5 10, stabilizer 1 3, lubricant 0.1 1, turpentine 0.1 2, and the material first adds PVC, CPE, TPV, PE and TPV to the material. The high-speed mixer mixes evenly, then adds soybean oil and trioctyl phthalate to the mixer at high speed, and then adds stabilizer, lubricant, toner and turpentine to the mixer. After 20 to 30 minutes of high-speed mixing, the material is sent to the granulator for granulation; the cable material of the invention has strong flexibility and can be widely used in computers, refrigerators, air conditioners and other settings. Equipped connection lines, especially for mobile phones, computers and other products.
【技术实现步骤摘要】
一种改善柔韧性的PVC材料
本专利技术属于PVC电缆料制备
，具体是一种改善柔韧性的PVC材料。
技术介绍
目前，市面上常见的电缆料外层均是采用PVC材料包覆，因为此种材料比较廉价，制备方法简单，但是在使用过程中容易出现不耐高温、低温、不耐老化、柔韧性差等问题。因此，在比较上档次的产品中，大到如电脑、空调、电视、冰箱、洗衣机等产品的电源线、连接线，小到耳机、鼠标、数据线等，均是采用价格比较高的XLPE电缆料来制备，但是生产成本将会大幅提升。因此，研发一种外表柔韧、耐候性好、耐老化性能优越的PVC材料，使其能够用于日常生活中常用电子产品的电缆料中，是降低日常电子产品成本，拓展PVC材料销路的有效办法。
技术实现思路
本专利技术的目的就是针对目前PVC材料柔韧性、耐候性及耐老化性能均比较差，不适合用于日常电子产品电缆料的问题，提供一种改善柔韧性的PVC材料。本专利技术的一种改善柔韧性的PVC材料，它是由下述重量份原料组成：PVC50-65CPE3-8PE3-8TPV5-10大豆油1-3邻苯三酸三辛酯5-10稳定剂1-3润滑剂0.1-1松节油0.1-1色粉0.1-2；...
【技术保护点】
1.一种改善柔韧性的PVC材料，其特征在于由下述重量份原料组成：PVC 50‑65 CPE 3‑8PE 3‑8 TPV 5‑10大豆油 1‑3 邻苯三酸三辛酯 5‑10稳定剂 1‑3 润滑剂 0.1‑1松节油 0.1‑1 色粉 0.1‑2；所述PVC材料...
【技术特征摘要】
1.一种改善柔韧性的PVC材料，其特征在于由下述重量份原料组成：PVC50-65CPE3-8PE3-8TPV5-10大豆油1-3邻苯三酸三辛酯5-10稳定剂1-3润滑剂0.1-1松节油0.1-1色粉0.1-2；所述PVC材料是首先将PVC、CPE、PE、TPV加入高速混合机中搅拌均匀，然后向混合机中加入大豆油、邻苯三酸三辛酯高速混合，并将混合机升温至60-65度，将物料高度混合15-20分钟，停机，再向混合机中...