The invention relates to a vanadium silver nickel metal oxide catalyst, a preparation method and its application. The catalyst comprises the following elements, or is basically composed of the following elements, or is composed of the following elements: Ag, V, Ni, O, and at least one additive metal M. It is preferred that the catalyst has the following general formula (I): AgaVbNicMdOe, where b/a is at least 1.0, c/a is 0.05-1.2, d/a is 0.01-0.58, e is the value required to satisfy the valence of elements other than oxygen atoms in general formula (I). The invention also relates to the application of the bulk catalyst and the component loading of the bulk catalyst in selective oxidation of hydrocarbons after an inert carrier.
【技术实现步骤摘要】
一种钒银镍金属氧化物催化剂、制备方法及其应用
本专利技术涉及一种钒银镍金属氧化物催化剂。更具体而言，本专利技术涉及本体型钒银镍金属氧化物催化剂、制备方法。本专利技术还涉及该本体催化剂和本体催化剂组分负载在惰性载体后在烃类选择氧化中的应用。
技术介绍
钒银金属氧化物具有良好的氧化性能，可以用于催化氧化甲苯生成苯甲酸和苯甲醛、邻二甲苯氧化合成苯酐、对二甲苯氧化合成对苯二甲酸、甲基吡啶氧化合成吡啶甲酸等。例如，Delaigle等将Ag掺杂到VOx/TiO2催化剂中，结果发现银与钒之间的协同作用降低了催化剂粒径，从而提高了催化剂的氧化性能（TopicsinCatalysis，2013年56卷18-20期1867-1874页）。BASF公司在CN200580009783.9、CN200480021531.3和CN99813146.6等专利中报道了V-Ag-O经过碱金属、碱土金属、Bi、Tl、Cu、Zn、Cd、Pb、Cr、Au、Al、Fe、Co、Ni、Mo、Nb、Ce、W、Mn、Ta、Pd、Pt、Ru和Rh修饰后作为活性组分负载于无孔载体上可以用于催化合成醛、羧酸和羧酸酐。专...
【技术保护点】
1.一种用于氧化烃类的催化剂，其包含以下元素、或基本上由以下元素组成、或由以下元素组成：Ag、V、Ni、O、和至少一种助剂金属M。
【技术特征摘要】
1.一种用于氧化烃类的催化剂，其包含以下元素、或基本上由以下元素组成、或由以下元素组成：Ag、V、Ni、O、和至少一种助剂金属M。2.根据权利要求1所述的催化剂，其特征在于所述助剂金属M选自碱金属、碱土金属、过渡元素、IB族、IIB族、IIIA族、IVA族和VA族的至少一种助剂金属M。3.根据权利要求1所述的催化剂，其特征在于所述助剂金属M选自Li、Na、K、Rb、Cs、Mg、Ca、Sr、Ba、Ti、Zr、Nb、Cr、W、Mn、Re、Fe、Ru、Co、Pd、Pt、Cu、Au、Zn、Cd、Al、Ga、In、Sn、Pb、Sb、Bi、La、Ce、Nd。4.根据权利要求1所述的催化剂，其特征在于所述催化剂具有如下通式（I）：AgaVbNicMdOe其中，b/a为至少1.0，c/a=0.05~1.2，d/a=0.01~0.58，e为满足通式(I)中氧原子之外的元素的化合价所需要的数值，M为所述助剂金属，所述的催化剂中钒元...
【专利技术属性】
技术研发人员：刘经伟，李泽壮，方晓江，杨爱武，王英武，