一种高合金铁基合金粉末及其配比方法技术

本发明专利技术涉及一种高合金铁基自熔性粉末，由下列重量份的原料制成：C碳2.1‑3%，Cr铬6‑8%，Mn锰0‑2%，Si硅1‑2%，Ni镍2‑4%，B硼2‑3%，Mo钼3‑5%，V钒0.2%‑0.4%，Fe铁55‑75%，通过本配方得到的产品可以保证合金层的质量，提高产品的耐磨性，提高产品表层的硬度，延长产品的寿命，同时减少合金粉末的使用量，节约材料成本，减少投入，具有很大的经济效益，同时也节约了时间提高了生产效率。

A High Alloy Ferroalloy Powder and Its Mixing Method

The present invention relates to a high alloy iron-based self-fluxing powder, which is made from the following raw materials: C C 2.1 3%, Cr Cr 6 8%, Mn 0 2%, Si Si 1 2%, Ni 2 4%, B 2 3%, Mo Mo 3 5%, V 0.2% 0.4%, Fe 55 75%. The product obtained by this formula can guarantee the quality of the alloy layer, improve the wear resistance of the product, improve the hardness of the product surface layer, and prolong the product. The life of the product, at the same time reducing the use of alloy powder, saving material costs, reducing investment, has great economic benefits, but also saves time to improve production efficiency.

【技术实现步骤摘要】
一种高合金铁基合金粉末及其配比方法
本专利技术涉及冶金行业用以提高金属表面材料的硬度，尤其涉及一种高合金铁基自熔性粉末及其配比方法。
技术介绍
应用在注塑机料管中，通过融化离心的工艺在料管内表面覆上一层合金，现有方案存在的问题主要是合金粉末在熔覆的过程中，合金层不均匀，硬度无法达到68HRC。目前已有的铁基粉末在应用上存在的主要问题是在熔覆过程中出现料筒合金层分布不均，硬度不能达到要求。
技术实现思路
对上述现有技术的现状，本专利技术所要解决的技术问题在于提供一种增加合金溶液的流动性，使合金层分布均匀，提高合金层的硬度，并保证合金层的综合力学性能的高合金铁基自熔性粉末。本专利技术解决上述技术问题所采用的技术方案为：一种高合金铁基自熔性粉末，由下列重量份的原料制成：C碳2.1-3%，Cr铬6-8%，Mn锰0-2%，Si硅1-2%，Ni镍2-4%，B硼2-3%，Mo钼3-5%，V钒0.2%-0.4%，Fe铁55-75%。一种高合金铁基自熔性粉末配比方法，每种配料按照顺序和时间间隔投放，熔炼温度在1400-1550度之间，出钢温度在1430-1520度之间。粉末在应用过程中，合金层厚度误差控制本文档来自技高网...

【技术保护点】
1.一种高合金铁基自熔性粉末，其特征在于，由下列重量份的原料制成：C碳2.1‑3%，Cr铬6‑8%，Mn锰0‑2%，Si硅1‑2%，Ni镍2‑4%，B硼2‑3%，Mo钼3‑5%，V钒0.2%‑0.4%， Fe铁55‑75%。

【技术特征摘要】
1.一种高合金铁基自熔性粉末，其特征在于，由下列重量份的原料制成：C碳2.1-3%，Cr铬6-8%，Mn锰0-2%，Si硅1-2%，Ni镍2-4%，B硼2-3%，Mo钼3-5%，V钒0.2%-0.4%，Fe铁55-75%。2.一种高...

【专利技术属性】
技术研发人员：周侃，李益明，邵翼虎，
申请(专利权)人：宁波华帆金属材料科技有限公司，
类型：发明
国别省市：浙江,33