The invention provides a binder for cubic boron nitride, a polycrystalline composite tool and a preparation method thereof. The binder includes metal aluminium, silicon dioxide, chromium oxide, titanium diboride and titanium nitride. Among them, aluminium oxide and silicon dioxide react to form alumina and silicon monomer during sintering process, the melting point of alumina is much higher than that of metal aluminium, and the silicon monomer has good thermal conductivity, such as: Therefore, the binder can effectively overcome the shortcomings of metal binder and ceramic binder. It can effectively improve the hardness, toughness and thermal conductivity of the Cubic Boron Nitride Polycrystalline Composite Tool and has wide adaptability in the process of preparing Cubic Boron Nitride Polycrystalline Composite Tool.
【技术实现步骤摘要】
一种立方氮化硼用粘结剂、聚晶复合刀具及其制备方法
本专利技术属于超硬材料领域，具体地，涉及一种立方氮化硼用粘结剂、聚晶复合刀具及其制备方法。
技术介绍
聚晶立方氮化硼是立方氮化硼颗粒和一定比例的粘结剂在高温高压下烧结而成的。粘结剂在合成聚晶立方氮化硼的过程中起着重要的作用，加入适量的粘结剂可以降低烧结温度和压力，并能改善烧结体的性能。聚晶立方氮化硼粘结剂主要有金属粘结剂和陶瓷粘结剂。其中，金属粘结剂通常在700～800℃软化，会导致聚晶立方氮化硼的耐磨性下降。陶瓷粘结剂具有较高的耐高温磨损和较强的抗化学磨损优点，但陶瓷在高温时导热性差，使切削温度集中在被加工材料上，使之软化。因此，开发一种粘结剂克服金属粘结剂的软化问题和陶瓷粘结剂的导热问题具有重要的现实意义。
技术实现思路
有鉴于此，本专利技术提供一种立方氮化硼用粘结剂、聚晶复合刀具及其制备方法，以解决上述问题。具体地，本专利技术采取如下技术方案：一种立方氮化硼用粘结剂，它包括以下质量份的组分：金属铝(Al)2～5份、二氧化硅(SiO2)21～50份、氧化铬(Cr2O3)24～38份、二硼化钛(TiB2)26～32份...
【技术保护点】
1. 一种立方氮化硼用粘结剂，其特征在于，它包括以下质量份的组分：金属铝 2～5份、二氧化硅 21～50份、氧化铬 24～38份、二硼化钛 26～32份和氮化钛 13～27份。
【技术特征摘要】
1.一种立方氮化硼用粘结剂，其特征在于，它包括以下质量份的组分：金属铝2～5份、二氧化硅21～50份、氧化铬24～38份、二硼化钛26～32份和氮化钛13～27份。2.根据权利要求1所述的粘结剂，其特征在于，它还包括以下质量份的组分：金属镁6～14份。3.根据权利要求2所述的粘结剂，其特征在于，它还包括以下质量份的组分：石墨烯微粉0.7～2.2份，所述石墨烯微粉的粒径为20～40nm。4.根据权利要求1～3任一项所述的粘结剂，其特征在于，它的平均粒径为200～300nm。5.一种立方氮化硼聚晶复合刀具，其...
【专利技术属性】
技术研发人员：王丽娜，周青，
申请(专利权)人：河南海纳德新材料有限公司，
类型：发明
国别省市：河南,41