The invention provides a binder, a cubic boron nitride polycrystalline sintering body and a preparation method thereof. The binder includes metal aluminium, silicon dioxide, metal chromium, titanium boride, titanium diboride, titanium silicide and titanium nitride. In the sintering process, metal aluminium can react with silicon dioxide to form alumina and silicon, and metal chromium can form chromium nitride with the promotion of titanium silicide and cubic boron nitride. Therefore, the binder can effectively overcome the shortcomings of metal binder and ceramic binder. It can effectively improve the hardness, toughness and thermal conductivity of polycrystalline cubic boron nitride in the process of preparing cubic boron nitride polycrystalline sinter, and has wide adaptability.
【技术实现步骤摘要】
一种结合剂、立方氮化硼聚晶烧结体及其制备方法
本专利技术属于超硬材料领域，具体地，涉及一种结合剂、立方氮化硼聚晶烧结体及其制备方法。
技术介绍
聚晶立方氮化硼是立方氮化硼颗粒和一定比例的结合剂在高温高压下烧结而成的。结合剂在合成聚晶立方氮化硼的过程中起着重要的作用，加入适量的结合剂可以降低烧结温度和压力，并能改善烧结体的性能。聚晶立方氮化硼结合剂主要有金属结合剂和陶瓷结合剂。其中，金属结合剂通常在700～800℃软化，会导致聚晶立方氮化硼的耐磨性下降。陶瓷结合剂具有较高的耐高温磨损和较强的抗化学磨损优点，但陶瓷在高温时导热性差，使切削温度集中在被加工材料上，使之软化。因此，开发一种结合剂克服金属结合剂的软化问题和陶瓷结合剂的导热问题具有重要的现实意义。
技术实现思路
有鉴于此，本专利技术提供一种一种结合剂、立方氮化硼聚晶烧结体及其制备方法，以解决上述问题。具体地，本专利技术采取如下技术方案：一种结合剂，它包括以下质量份的组分：金属铝(Al)7～12份、二氧化硅(SiO2)27～43份、金属铬(Cr)3～5份、硼化钛(TiB)2～7份、二硼化钛(TiB2)30～40份、...
【技术保护点】
1. 一种结合剂，其特征在于，它包括以下质量份的组分：金属铝 7～12份、二氧化硅 27～43份、金属铬 3～5份、硼化钛 2～7份、二硼化钛 30～40份、硅化钛8～12份和氮化钛 5～10份。
【技术特征摘要】
1.一种结合剂，其特征在于，它包括以下质量份的组分：金属铝7～12份、二氧化硅27～43份、金属铬3～5份、硼化钛2～7份、二硼化钛30～40份、硅化钛8～12份和氮化钛5～10份。2.根据权利要求1所述的结合剂，其特征在于，它的平均粒径为200～300nm。3.根据权利要求1或2所述的结合剂，其特征在于，它还包括石墨烯微粉0.5～2.5份，所述石墨烯微粉的粒径为32～54nm。4.一种立方氮化硼聚晶烧结体，其特征在于，它包括以下质量份的原料：立方氮化硼7...
【专利技术属性】
技术研发人员：王丽娜，周青，
申请(专利权)人：河南海纳德新材料有限公司，
类型：发明
国别省市：河南,41