The invention provides a binder, a polycrystalline cubic boron nitride composite material and a preparation method thereof. The binder includes component metal aluminum, silicon dioxide, silicon carbide, silicon nitride and titanium nitride. Among them, aluminum oxide and silicon dioxide react during sintering process to form alumina and silicon monomer. The melting point of alumina is much higher than that of aluminium metal, and the silicon monomer has good thermal conductivity, such as: Therefore, the binder can effectively overcome the shortcomings of metal binder and ceramic binder. When used in the preparation of polycrystalline cubic boron nitride composites, it can effectively improve the hardness, toughness and thermal conductivity of cutting tools, and has broad adaptability.
【技术实现步骤摘要】
一种粘结剂、聚晶立方氮化硼复合材料及其制备方法
本专利技术属于超硬材料领域，具体地，涉及一种粘结剂、聚晶立方氮化硼复合材料及其制备方法。
技术介绍
聚晶立方氮化硼是立方氮化硼颗粒和一定比例的粘结剂在高温高压下烧结而成的。粘结剂在合成聚晶立方氮化硼的过程中起着重要的作用，加入适量的粘结剂可以降低烧结温度和压力，并能改善烧结体的性能。聚晶立方氮化硼粘结剂主要有金属粘结剂和陶瓷粘结剂。其中，金属粘结剂通常在700～800℃就会软化，会导致聚晶立方氮化硼的耐磨性下降。陶瓷粘结剂具有较高的耐高温磨损和较强的抗化学磨损优点，但陶瓷在高温时导热性差，使切削温度集中在被加工材料上，使之软化。因此，开发一种粘结剂克服金属粘结剂的软化问题和陶瓷粘结剂的导热问题具有重要的现实意义。
技术实现思路
有鉴于此，本专利技术提供一种粘结剂、聚晶立方氮化硼复合材料及其制备方法，以解决上述问题。具体地，本专利技术采取如下技术方案：一种粘结剂，它包括以下质量份的组分：金属铝（Al）2～5份、二氧化硅（SiO2）13～35份、碳化硅（SiC）30～40份、氮化硅（Si3N4）10～15份和氮化钛（TiN）...
【技术保护点】
1. 一种粘结剂，其特征在于，它包括以下质量份的组分：金属铝 2～5份、二氧化硅 13～35份、碳化硅 30～40份、氮化硅 10～15份和氮化钛 15～30份。
【技术特征摘要】
1.一种粘结剂，其特征在于，它包括以下质量份的组分：金属铝2～5份、二氧化硅13～35份、碳化硅30～40份、氮化硅10～15份和氮化钛15～30份。2.根据权利要求1所述的粘结剂，其特征在于，它的平均粒径为200～300nm。3.根据权利要求1或2所述的粘结剂，其特征在于，它还包括石墨烯微粉0.5～2.5份，所述石墨烯微粉的粒径为15～42nm。4.一种聚晶立方氮化硼复合材料，其特征在于，它包括以下质量份的原料：立方氮化硼65～87份和权利...