A new kind of diamond film coating
The present invention discloses a new kind of diamond film coating field, including the combination of stainless steel and metal surface of the base layer and function layer is located in the coating surface of the diamond film, the base for the Cr layer, the functional layer of diamond-like carbon layer: the first transition layer and second transition layer is also arranged between the base and the functional layer, the first layer is located in the functional layer below the WC layer, the second layer is located in the base layer and the transition layer between the first layer, CrWC. The technical effect is that under the premise of ensuring DLC coating hardness, wear resistance of DLC coating with 5 ~ 10 fold increase, not easily from the surface of the substrate as stainless steel metal loss, functional layer deposition time is only the same thickness between the deposition decreased by 15% ~ 20%.
【技术实现步骤摘要】
一种新型类金刚石薄膜涂层
本专利技术涉及镀膜领域的一种新型类金刚石薄膜涂层。
技术介绍
在纺织、汽车、手表机芯等行业的零部件要求具有较高的硬度和耐磨性，为了达到生产商的硬度和耐磨性要求，必须对零件表面进行涂层处理，以使零部件表面达到所需要的耐摩擦和耐腐蚀性能。根据一些相关标准，零部件表面的薄膜涂层必须通过300℃的淬火实验和24种化学品药剂腐蚀测试等严酷要求，还必须经过1000次橡皮摩擦测试不能有划痕，薄膜涂层的硬度也要求达到2000-3000HV。目前常用的薄膜涂层为在不锈钢金属表面直接涂覆钛底层，再镀类金刚石层，即Ti+C层，采用的工艺为物理气相沉积工艺，这样的工艺，因为钛底层与类金刚石层的性能差异，致使薄膜涂层临界载荷偏低，应用上有限制。而且要求的薄膜涂层的厚度大。
技术实现思路
本专利技术的目的是为了克服现有工艺的不足，提供一种新型类金刚石薄膜涂层，其在保证硬度的前提下，耐磨性能有了显著提高，而且沉积时间短。实现上述目的的一种工艺方案是：一种新型类金刚石薄膜涂层，包括与不锈钢金属表面结合的基层以及位于该类金刚石薄膜涂层表面的功能层，所述基层为Cr层，所述功能层...
【技术保护点】
一种新型类金刚石薄膜涂层，包括与不锈钢金属表面结合的基层以及位于该类金刚石薄膜涂层表面的功能层，所述基层为Cr层，所述功能层为类金刚石层；其特征在于：所述基层和所述功能层之间还设有第一过渡层和第二过渡层，所述第一过渡层位于所述功能层的下方，为WC层，所述第二过渡层位于所述基层和所述第一过渡层之间，为CrWC层。
【技术特征摘要】
1.一种新型类金刚石薄膜涂层，包括与不锈钢金属表面结合的基层以及位于该类金刚石薄膜涂层表面的功能层，所述基层为Cr层，所述功能层为类金刚石层；其特征在于：所述基层和所述功能层之间还设有第一过渡层和第二过渡层，所述第一过渡层位于所述功能层的下方，为WC层，所述第二过渡层位于所述基层和所述第一过渡层之间，为CrWC层。2.根据权利要求1所述的一种新型...