The invention discloses a high strength injectable bioactive material, which belongs to the field of biomedical materials. Including nano-silica, tricalcium silicate and curing solution; the mass ratio of tricalcium silicate powder, nano-silica and curing solution is 1:0.01 0.05 0.4 0.8. The curing time of the bioactive material is 30 55 minutes, and the compressive strength is 61 77 MPa in 7 days. It can also induce the formation of hydroxyapatite. Compared with the existing materials, the materials of the invention have excellent mechanical properties, rapid curing, excellent biological activity and other characteristics. The invention also discloses a preparation method of a high strength injectable bioactive material.
【技术实现步骤摘要】
一种高强度可注射型生物活性材料及其制备方法
本专利技术涉及生物医用材料领域，特别涉及一种高强度可注射型生物活性材料及其制备方法。
技术介绍
近年来，大量研究表明，一些含硅-钙生物活性材料以及硅酸钙生物陶瓷表面在体内、外均能诱导类骨磷灰石的生成，能够促进生物材料与骨组织键合。此外，含硅-钙生物活性材料释放的硅、钙离子能够刺激骨髓基质干细胞向成骨细胞分化并激活细胞基因表达。硅酸三钙（TricalciumSilicate，TCS）是一种含硅、钙元素的生物活性材料，在人体骨组织和牙缺损修复治疗中，可在缺损部位进行填充修复。TCS粉体中加入适量的固化液制备的糊状物具有任意塑形，自行固化等特点。当TCS粉体与模拟体液接触时，能够在其表面形成纳米级的碳酸型类骨磷灰石层。该沉积的碳酸型类骨磷灰石层具有与人体骨中纳米级针状磷灰石晶体相同的结构，从而保证了与人体骨组织中的胶原键合和外延生长。TCS是波特兰水泥的主要成分，它也是牙科填充材料MineralTrioxideAggregate(MTA，三氧化矿物凝聚体)的主要成分，MTA主要由TCS、硅酸二钙、铝酸三钙、铁铝酸四钙以及氧化铋...
【技术保护点】
1.一种高强度可注射型生物活性材料，其特征在于，由以下组份组成，包括纳米级二氧化硅、硅酸三钙粉体和固化液；所述硅酸三钙粉体、纳米级二氧化硅和固化液的质量比为1：0.01‑0.05：0.4‑0.8。
【技术特征摘要】
1.一种高强度可注射型生物活性材料，其特征在于，由以下组份组成，包括纳米级二氧化硅、硅酸三钙粉体和固化液；所述硅酸三钙粉体、纳米级二氧化硅和固化液的质量比为1：0.01-0.05：0.4-0.8。2.根据权利要求1所述的一种高强度可注射型生物活性材料，其特征在于，所述固化液为含有氯化钙和梳形聚羧酸的蒸馏水或去离子水；所述氯化钙占固化液的质量百分数含量为1-25%，所述梳形聚羧酸占固化液的质量百分数含量为0.1-1%；所述梳形聚羧酸含有长侧链和短主链。3.根据权利要求1或2所述的一种高强度可注射型生物活性材料，其特征在于，所述纳米级二氧化硅颗粒粒径为15-50nm，所述硅酸三钙粉体颗粒粒径为0.1-100µm，所述硅酸三钙粉体纯度为95%以上。4.根据权利要求3所述的一种高强度可注射型生物活性材料，其特征在于，所述硅酸三钙粉体颗粒粒径为0.1-10µm。5.一种高强度可注射型生物活性材料的制备方法，其特征在于，具体包括以下步骤：（1）硅酸三钙粉体的制备首先采用湿化学法制备硅酸三钙前驱体，然后将硅酸三钙前驱体经高温煅烧、球磨得到硅酸三钙粉体；（2）按比例称取所述硅酸三钙粉体及反应所需的固化液，向固化液中加入纳米级二氧化硅，通过超声振动...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。