The invention belongs to the technical field of curved surface sheet metal, and discloses a curved surface sheet metal shell and its preparation method, which adopts blank holder welding. The blank holder is continuous blank holder, the blank holder height is 2 15mm, and the blank holder parts are butted together. The blank holder is joined together by welding, riveting and spot welding. Because of welding, riveting, riveting and spot welding, the blank holder is joined together. Spot welding and other parts are operated at the blank holder. There is no weld on the outer surface of the metal shell. The joint of the blank holder of the metal shell has higher strength because of the blank holder and other reasons. After the thin metal shell of the curved surface of the invention is joined by blank holder, there are no solder joints on the outer surface of the product. After the blank holder is joined together, the strength becomes very large, and the appearance and service life of the product are well guaranteed.
【技术实现步骤摘要】
一种采用压边焊接的曲面薄板金属外壳及其制备方法
本专利技术属于曲面薄板金属
，尤其涉及一种采用压边焊接的曲面薄板金属外壳及其制备方法。
技术介绍
目前，业内常用的现有技术是这样的：目前没有与本方案相近的工艺：方法一直接焊接：曲线连接部位不起边，直接把曲面曲线处对在一起焊接，这样的焊接工艺造成焊点外露，特别不美观，并且容易生锈。方法二单点铆接：曲线连接部位预留几个长约15mm，宽约20mm的连接条，两个曲面对接在一起，使用连接条把另外一个曲面连接在一起。目前常用技术：(1)直接焊接，问题：产品易产生焊孔，外表面有焊点，焊接速度慢，容易腐蚀，不美观，影响产品使用寿命等问题；(2)单点铆接，问题：连接面有缝隙，产品强度差，碰撞后容易开裂，不美观，产品使用寿命低。综上所述，现有技术存在的问题是：现有技术中，直接焊接，产品外面面有焊点，容易腐蚀，影响产品使用寿命；单点铆接，连接面有缝隙、产品强度差，碰撞后容易开裂，不美观，产品使用寿命低。解决上述技术问题的难度和意义：曲面薄板连接难度大，特别是对防腐、美观、强度要求较高的产品，一半的工艺焊接、铆接工艺都有其重大缺陷，(...
【技术保护点】
1.一种采用压边焊接的曲面薄板金属外壳的制备方法，其特征在于，所述采用压边焊接的曲面薄板金属外壳的制备方法包括：裁板：金属薄板按照图形要求裁剪；压边：连接在一起的曲面部位进行压边，压边角度为90°；卷板：压好边的金属薄板卷成弧形；焊接：将连接在一起的压边对在一起，使用焊接或铆接技术，把压边连接在一起。
【技术特征摘要】
1.一种采用压边焊接的曲面薄板金属外壳的制备方法，其特征在于，所述采用压边焊接的曲面薄板金属外壳的制备方法包括：裁板：金属薄板按照图形要求裁剪；压边：连接在一起的曲面部位进行压边，压边角度为90°；卷板：压好边的金属薄板卷成弧形；焊接：将连接在一起的压边对在一起，使用焊接或铆接技术，把压边连接在一起。2.如权利要求1所述的采用压边焊接的曲面薄板金属外壳的制备方法，其特征在于，压边高度2-15mm。3.一种...