The present invention discloses a special environmental-friendly slag cleaner for alloy and its processing method, which includes the following steps: (1) selecting raw materials according to weight percentage: silica 20_25%, sodium oxide 20_30%, titanium dioxide 8_16%, cryolite 5_15%, grass ash 10_18%, carbon powder 5_15%; (2) weighing raw materials, mixing and stirring evenly; (3) putting mixed raw materials into crusher to break. Crushing; (4) The crushed raw materials are dried, air-cooled to room temperature, sealed and preserved. The slag cleaning agent processed by the invention is a granular product without the influence of dust, which will not harm the air, machinery or human body, and is more environmentally friendly.
【技术实现步骤摘要】
一种合金专用环保型清渣剂及其加工方法
本专利技术涉及铝合金清渣剂，具体涉及一种合金专用环保型清渣剂及其加工方法。
技术介绍
合金在冶炼过程中，为了避免杂质的会合金的金属性能产生影响，需要使用清渣剂来进行清渣精炼，但是现有技术的清渣效果不够好，对环境会产生污染，也影响了合金的金属性能。
技术实现思路
本专利技术为解决上述问题，提供了一种合金专用环保型清渣剂及其加工方法，具体包括如下步骤：(1)根据重量百分比选取原料：二氧化硅20-25％，氧化钠20-30％，二氧化钛8-16％，冰晶石5-15％，草木灰10-18％，碳粉5-15％；(2)称取原料后混合搅拌均匀；(3)将混合原料投入破碎机破碎；(4)将破碎后的原料进行烘干，空冷至室温，密封保存。进一步的，步骤(3)中，破碎后过筛80-100目。进一步的，步骤(4)中，烘干温度为80-100℃，烘干时间为15-20min。本专利技术的有益效果是：采用本专利技术加工的清渣剂，成品为颗粒产品，没有粉尘的影响，不会对空气、机器或者人体产生危害，更加环保。具体实施方式实施例1一种合金专用环保型清渣剂及其加工方法，具体包括如下步骤：(1)根据重量百分比选取原料：二氧化硅20％，氧化钠20％，二氧化钛8％，冰晶石5％，草木灰10％，碳粉5％；(2)称取原料后混合搅拌均匀；(3)将混合原料投入破碎机破碎；(4)将破碎后的原料进行烘干，空冷至室温，密封保存。其中，步骤(3)中，破碎后过筛80目。步骤(4)中，烘干温度为80℃，烘干时间为15min。实施例2一种合金专用环保型清渣剂及其加工方法，具体包括如下步骤：(1)根据重量百分比选...
【技术保护点】
1.一种合金专用环保型清渣剂及其加工方法，其特征在于，具体包括如下步骤：(1)根据重量百分比选取原料：二氧化硅20‑25％，氧化钠20‑30％，二氧化钛8‑16％，冰晶石5‑15％，草木灰10‑18％，碳粉5‑15％；(2)称取原料后混合搅拌均匀；(3)将混合原料投入破碎机破碎；(4)将破碎后的原料进行烘干，空冷至室温，密封保存。
【技术特征摘要】
1.一种合金专用环保型清渣剂及其加工方法，其特征在于，具体包括如下步骤：(1)根据重量百分比选取原料：二氧化硅20-25％，氧化钠20-30％，二氧化钛8-16％，冰晶石5-15％，草木灰10-18％，碳粉5-15％；(2)称取原料后混合搅拌均匀；(3)将混合原料投入破碎机破碎；(4)将破碎后...
【专利技术属性】
技术研发人员：梁建龙，
申请(专利权)人：徐州特普勒金属科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。