The invention provides a winding method for lithium battery separator, which can eliminate or reduce the problems of the implosion and warping of the separator winding, and the winding is neat. A winding method of lithium battery separator includes the following steps: A attaches rubber strip to the roll surface of the winding roll, and rolls the separator on the roll surface with rubber strip; B adjusts the distance between the winding roll and the transmission roll; C blank holder to flatten the edge of the separator. In step A, at least one group of strips is attached to the roll surface of the winding roll, and each group of strips is arranged on the roll surface of the winding roll at equal intervals along the circumference direction of the winding roll.
【技术实现步骤摘要】
锂电池隔膜的收卷方法
本专利技术属于锂电池隔膜制造领域,具体涉及一种锂电池隔膜的非接触式收卷方法。
技术介绍
传统隔膜或薄膜行业(如锂电池隔膜)在收卷机上收卷产品的方式一般为接触式收卷和非接触式收卷,而接触式收卷主要靠张力来控制收卷薄膜的质量,非接触式也就是间隙式收卷,要控制收卷的张力。然而,收卷后的薄膜产品的厚度均匀性总是有偏差,无法保证收卷的产品不会产生爆筋,变形,收卷不齐,翘边等缺陷。
技术实现思路
针对上述问题,本专利技术的目的是提供一种锂电池隔膜的收卷方法,消除或降低隔膜收卷内爆以及翘边的问题,收卷整齐。为达到上述目的,本专利技术采用的技术方案为:一种锂电池隔膜的收卷方法,包括如下步骤:A在收卷辊的辊面贴附胶条,将隔膜收卷于贴附有胶条的辊面上;B调节收卷辊和传动辊之间的间距;C压边以将隔膜的边缘展平。优选地,步骤A中,收卷辊的辊面上贴附有至少一组胶条,每组胶条沿收卷辊的圆周方向等间隔地排列于收卷辊的辊面上。优选地,步骤A中,胶条为邵氏硬度45°~60°的橡胶胶条。优选地,步骤B中,调节收卷辊和传动辊之间的间距为50~200mm。优选地,步骤C中,通过将压缩空气吹拂到隔膜边缘以抚平翘边。更优选地,步骤C中,通过高压喷嘴将压缩空气吹拂到隔膜边缘。进一步地,所述压缩空气的压力为2~4公斤。更进一步地,所述高压喷嘴的口径为0.5~2mm。本专利技术采用上述技术方案,相比现有技术具有如下优点:通过在收卷辊的辊面上贴附一定硬度的胶条来很好的解决了爆筋,变形的问题;适当的调整辊与辊之间的间隙则很好的解决了收卷不齐的问题;压边以避免收卷翘边。具体实施方式下面对本专利 ...
【技术保护点】
1.一种锂电池隔膜的收卷方法,其特征在于,包括如下步骤:A在收卷辊的辊面贴附胶条,将隔膜收卷于贴附有胶条的辊面上;B调节收卷辊和传动辊之间的间距;C压边以将隔膜的边缘展平。
【技术特征摘要】
1.一种锂电池隔膜的收卷方法,其特征在于,包括如下步骤:A在收卷辊的辊面贴附胶条,将隔膜收卷于贴附有胶条的辊面上;B调节收卷辊和传动辊之间的间距;C压边以将隔膜的边缘展平。2.根据权利要求1所述的收卷方法,其特征在于:步骤A中,收卷辊的辊面上贴附有至少一组胶条,每组胶条沿收卷辊的圆周方向等间隔地排列于收卷辊的辊面上。3.根据权利要求1所述的收卷方法,其特征在于:步骤A中,胶条为邵氏硬度45°~60°的橡胶胶条。4.根据权利要求1所...