A one-step method for preparing flower-shaped silver particles with controllable branch length belongs to the technical field of nanomaterials preparation. The specific steps are as follows: adding silver nitrate aqueous solution and silane coupling agent to ultra-pure water under magnetic stirring condition, mixing and stirring for 90 seconds, adding ascorbic acid to the system, and continuing to react at room temperature for 3-5 minutes to obtain flower-shaped silver particles. The method of the invention can simply prepare silver particles with different flower length by adding different amounts of APTES, and has the characteristics of simple operation, mild reaction conditions, low cost and environment friendliness.
【技术实现步骤摘要】
一种一步法制备枝长可控的花状银粒子的方法
本专利技术属于纳米材料制备的
，特别涉及一种一步法制备枝长可控的花状银粒子的方法。
技术介绍
近年来，贵金属纳米材料一直是人们的研究热点，由于其独特的光学、电学、催化等性质，被广泛应用。其中，银纳米颗粒由于其在可见光区具有强的等离子体效应，被广泛应用于传感器、生物、医疗等多个领域。而银纳米花由于其各向异性的性质更是被广泛关注。银纳米颗粒的性质与其形貌有着很大的关系，而花枝的长度是影响花状银粒子形貌的重要因素，所以实现对花状银粒子花枝长度的调控十分重要。目前，关于花状银粒子的制备虽然已经有了一些报道，但是对于枝长的调控仍然存在一些问题。MaXinfu用半胱氨酸在碱性条件下还原硝酸银制备花状银粒子，但是需要在70℃的高温条件下、4h以后才能完成反应，存在高温反应及反应时间长的问题(MaXinfu,GuoQingquan,XieYu,MaHaixiang,ChemicalPhysicsLetters652(2016)148–151.)；XiaoShuangShen,GuanZhongWang等用抗坏血酸钠在30℃水浴中还原...
【技术保护点】
1.一种一步法制备枝长可控的花状银粒子的方法，具体步骤如下：在磁力搅拌条件下，向超纯水中加入硝酸银水溶液和硅烷偶联剂，混合搅拌90s后，向体系中加入还原剂抗坏血酸，在室温条件下继续反应3～5min，得到花状银粒子；在所有反应物混合后的体系中，硝酸银的浓度为0.25mM；硅烷偶联剂与银离子的摩尔比为2～8:1；还原剂抗坏血酸与硝酸银的摩尔比为1:1。
【技术特征摘要】
1.一种一步法制备枝长可控的花状银粒子的方法，具体步骤如下：在磁力搅拌条件下，向超纯水中加入硝酸银水溶液和硅烷偶联剂，混合搅拌90s后，向体系中加入还原剂抗坏血酸，在室温条件下继续反应3～5min，得到花状银粒子；在所有反应物混合后的体系中，硝酸银的浓度为0.25mM；硅烷偶联剂与银离子的摩尔比为2～8:1；还原剂抗坏血酸与硝酸银的摩尔比为1:1。2.根据权利要求1所述的一种一步法制备枝长可控的花状银粒子的方法，其特征在于，所述的硅烷偶联剂是3-氨丙...