The invention relates to a chlorinated butyl rubber piston for pre-filling syringe and its preparation process, belonging to the field of medicinal bottle stopper materials, which is prepared from 100 parts of chlorinated butyl rubber, 0.8 2 parts of accelerator, 0.3 2 parts of acid absorbent, 20 40 parts of calcined kaolin, 20 30 parts of magnesium powder, 1 3 parts of polyisobutylene, 2 3 parts of titanium white, 0.1 0.3 parts of carbon black. \u3002 The invention relates to a chlorinated butyl rubber piston for pre-filling syringe and its preparation method; the prepared product has good compatibility with medicines to ensure the stability of medicines; the accelerator DB is used as a vulcanizing agent to produce medical rubber plug products; when the product is in long-term contact with medicines, the small molecular substances in the piston will not migrate to medicines and will not cause the quality and safety of medicines. All hidden dangers.
【技术实现步骤摘要】
预灌封注射器用氯化丁基橡胶活塞及其制备工艺
本专利技术涉及一种预灌封注射器用氯化丁基橡胶活塞及其制备工艺，属于药用瓶塞材料领域。
技术介绍
预灌封注射器是将注射药物直接灌装在玻璃或塑料的注射器中，且注射器上安装有注射针头，将注射器和药液包装容器合二为一，使用时直接注射，节约时间，使用更加方便；因使用时无交叉感染，避免使用稀释液后反复抽吸造成的二次污染，所以更安全。由于活塞作为预灌封注射器包装系统组成部分，在药物储存过程中长期与药物接触，这就决定了除了具备使用性能外，对药物相容性、洁净度也有了更高的要求。但传统配方体系(例如常用的树脂硫化体系)药物相容性与洁净度差，很难满足预灌封注射器活塞的要求。促进剂DB已在橡胶工业中证实是一种不含亚硝胺，不喷霜的环保型促进剂，常见作为促进剂应用于三元乙丙橡胶以及天然橡胶制品配方中，但在文献中未见用作硫化剂报道，特别是医用橡胶生产中未见使用先例。综上所述目前领域存在以下不足之处：1、目前常用的树脂硫化体系生产的氯化丁基橡胶活塞，在化学性能检测中澄清度不良，容易导致胶塞与药品接触时，使存在污染药品的风险；2、目前常用的树脂硫化体系生...
【技术保护点】
1.一种预灌封注射器用氯化丁基橡胶活塞，其特征在于由以下质量份数的原料制备而成；
【技术特征摘要】
1.一种预灌封注射器用氯化丁基橡胶活塞，其特征在于由以下质量份数的原料制备而成；氯化丁基橡胶100促进剂0.8-2吸酸剂0.3-2煅烧高岭土20-40镁强粉20-30聚异丁烯1-3钛白粉2-3炭黑0.1-0.3。2.根据权利要求1所述的预灌封注射器用氯化丁基橡胶活塞，其特征在于所述的：促进剂为N,N’-二正丁基硫脲。3.根据权利要求1所述的预灌封注射器用氯化丁基橡胶活塞，其特征在于所述的：吸酸剂为氧化镁。4.根据权利要求1所述的预灌封注射器用氯化丁基橡胶活塞，其特征在于所述的：预灌封注射器用氯化丁基橡胶活塞的制备工艺如下：原料配合→混炼→预成型→硫化成型→除边→清洗...
【专利技术属性】
技术研发人员：孟凡平，逯纪伟，杜彬，
申请(专利权)人：山东省药用玻璃股份有限公司，
类型：发明
国别省市：山东,37