The invention relates to the technical field of Engineering materials, in particular to a kind of cement for overlapping bentonite waterproof blankets, which is made from the following weight parts of raw materials: asphalt 60 80, emulsifier 30 40, sodium-based bentonite 20 25, plasticizer 5 8, cold-resisting agent 2 5, ultraviolet-resisting agent 2 3, antioxidant 3 5. The invention overcomes the shortcomings of existing technology and utilizes leaching. Green, emulsifier, sodium-based bentonite, plasticizer, cold-resistant agent, anti-ultraviolet ray agent and antioxidant are used to make bentonite waterproof blanket lapping mortar. The bentonite mortar made by the invention has strong cohesion, does not occur dry cracking and shedding phenomenon after the cement is applied, so that the bentonite waterproof blanket has better waterproof and impermeability, and has cold resistance and oxidation resistance. It has low cost, good bonding effect and is suitable for popularization.
【技术实现步骤摘要】
膨润土防水毯搭接用胶泥
本专利技术涉及工程材料
，具体属于膨润土防水毯搭接用胶泥。
技术介绍
目前行业内膨润土防水毯搭接的处理通常采用的是膨润土颗粒和水按一定比例配制出来的膨润土胶泥。这种胶泥需要现场配置，且需要尽快用完，否则胶泥就会变干硬，无法继续使用。另外，这种胶泥涂抹后很容易失水造成干裂、脱落的现象，直接影响到膨润土防水毯的防水防渗效果。
技术实现思路
本专利技术的目的是提供了一种膨润土防水毯搭接用胶泥，克服了现有技术的不足，利用沥青，乳化剂，钠基膨润土，增塑剂，抗寒剂，抗紫外线剂，抗氧化剂，制成膨润土防水毯搭接用胶泥，解决现有胶泥容易失水造成干裂、脱落，直接影响到膨润土防水毯的防水防渗效果的缺点。为解决上述问题，本专利技术所采取的技术方案如下：膨润土防水毯搭接用胶泥，由下列重量份的原料制成：沥青60-80份，乳化剂30-40份，钠基膨润土20-25份，增塑剂5-8份，抗寒剂2-5份，抗紫外线剂2-3份，抗氧化剂3-5份。进一步，由下列重量份的原料制成：沥青70份，乳化剂32份，钠基膨润土22份，增塑剂6份，抗寒剂3份，抗紫外线剂2.5份，抗氧化剂3.2份...
【技术保护点】
1.膨润土防水毯搭接用胶泥，其特征在于：由下列重量份的原料制成：沥青 60‑80份，乳化剂30‑40份，钠基膨润土 20‑25份，增塑剂 5‑8份，抗寒剂2‑5份，抗紫外线剂2‑3份，抗氧化剂3‑5份。
【技术特征摘要】
1.膨润土防水毯搭接用胶泥，其特征在于：由下列重量份的原料制成：沥青60-80份，乳化剂30-40份，钠基膨润土20-25份，增塑剂5-8份，抗寒剂2-5份，抗紫外线剂2-3份，抗氧化剂3-5...
【专利技术属性】
技术研发人员：程玮，赵双，
申请(专利权)人：安徽中路工程材料有限公司，
类型：发明
国别省市：安徽,34