The invention discloses a water-borne high solid content waterproof sealing paste and a preparation method thereof, comprising the following raw material components of weight percentage: emulsified asphalt 25~40, self crosslinking acrylate emulsion 25~35, talcum powder 30~45, regulator 0.2~1.0, water 2~5, cellulose ether 0.1~0.5, mineral oil defoamer 0.3~0.8. The waterproof sealing paste provided by the invention is made of self crosslinking acrylic emulsion modified emulsified asphalt, which has good adhesion, heat resistance, water resistance and mechanical strength, is suitable for bonding various base surfaces, and has high solid content and short drying time, which is favorable for rapid construction. Total solid content; AMP_95 as a regulator can simultaneously adjust the wettability, dispersion effect and maintain the stability of pH value of the sealant.
【技术实现步骤摘要】
一种水性高固含量防水密封膏及其制备方法
本专利技术涉及防水建筑材料，具体涉及一种水性高固含量防水密封膏及其制备方法。
技术介绍
雨水渗透是建筑工程的通病，过多过久地雨水渗透会给建筑带来难以修复的损伤，影响建筑的寿命以及状态，现代建筑结构趋于复杂，防水问题一直是影响建筑使用寿命不容忽视的因素。除了楼层墙面的整体防水，各类塑料穿墙管道、金属管与混凝土交接处、阴阳角等节点部位的结构不规则，界面多样化，热膨胀收缩系数不一致使其在防水材料的选择和施工上存在一定难度。随着建筑行业和材料的发展，针对节点部位防水密封问题，已经发展出多种实用的材料，如聚氨酯密封胶、硅酮密封胶、聚硫橡胶等各种密封材料。但这些材料施工要求严格，在潮湿基面难与基面进行粘接，只对一种基面有效粘接，对多种基面如塑料管道、金属、玻璃、混凝土等的粘接不好。针对这类问题，市面上也出现了可在湿润环境下进行施工的水性防水密封膏，性能优良，如水性丙烯酸类、改性乳化沥青类等，只对基面进行清理后多次涂刷即可，但水性密封膏只有在其干固后才具有粘接和防水性能，其干固速度取决于内部水分的挥发。目前，水性防水密封膏的固含量多数不高...
【技术保护点】
1.种水性高固含量防水密封膏，其特征在于，包括如下重量百分数的各原料组分：乳化沥青 25~40自交联丙烯酸酯乳液 25~35滑石粉 30~45调节剂 0.2~1.0水 2~5纤维素醚 0.1~0.5矿物油消泡剂 0.3~0.8。
【技术特征摘要】
1.种水性高固含量防水密封膏，其特征在于，包括如下重量百分数的各原料组分：乳化沥青25~40自交联丙烯酸酯乳液25~35滑石粉30~45调节剂0.2~1.0水2~5纤维素醚0.1~0.5矿物油消泡剂0.3~0.8。2.根据权利要求1所述的一种水性高固含量防水密封膏，其特征在于，包括如下重量百分数的各原料组分：乳化沥青34自交联丙烯酸酯乳液30滑石粉32分散剂0.5水2.8纤维素醚0.2矿物油消泡剂0.5。3.根据权利要求1所述的一种水性高固含量防水密封膏，其特征在于，所述自交联丙烯酸酯乳液固含量为65%~85%。4.根据权利要求1所述的一种水性高固含量防水密封膏，其特征在于，所述乳化沥青固含量为65%~75%。5.根据权利要求1所述的一种水性高固含量...
【专利技术属性】
技术研发人员：刘勤，龚兴宇，杨小育，欧志荣，
申请(专利权)人：南通科顺建筑新材料有限公司，
类型：发明
国别省市：江苏,32