高黏不粘轮粘层油及其制备方法技术

本发明专利技术公开了一种高黏不粘轮粘层油，由下列重量比例的各组分组成：基质沥青：有机高分子化合物：橡胶油：植物油酸＝60～90：5～15：2～8：9～18。本发明专利技术还公开了上述高黏不粘轮粘层油的制备方法和使用方法。本发明专利技术所生产的高黏不粘轮粘层油施工方便，普通洒布车即可进行施工；多用途：替代普通黏层，不必提前洒布，提高施工效率；用于超薄罩面，不必采用专门的一体化摊铺设备；还可用于水泥铺装层的防水粘结层。

Viscous Oil of High Viscosity Non-Viscous Wheel and Its Preparation Method

The invention discloses a high viscous non-stick wheel viscous oil, which is composed of the following components in weight ratio: base asphalt: organic macromolecule compound: rubber oil: vegetable oleic acid = 60-90:5-15:2-8:9-18. The invention also discloses the preparation method and the use method of the high viscous non-stick wheel viscous oil. The high-viscous non-stick wheel adhesive layer oil produced by the invention is convenient for construction and can be constructed by common spraying truck; multi-purpose: instead of common sticky layer, it does not need to spray ahead of time to improve construction efficiency; it is used for ultra-thin cover without using special integrated paving equipment; and it can also be used for waterproof bonding layer of cement pavement.

【技术实现步骤摘要】
高黏不粘轮粘层油及其制备方法
本专利技术涉及化工产品制备领域，特别涉及一种高黏不粘轮粘层油及其制备方法。
技术介绍
粘层油作为沥青层之间的粘结层，众多研究表明，对沥青路面的使用性能和使用寿命都有很重要的影响，目前常用的粘层油主要为乳化沥青体系和热沥青体系。其主要缺点是：1、粘结强度较低；2、喷洒固化需要较长的时间；3、喷洒固化后，极易被施工车辆轮胎带走，起不到有效粘接上下两层沥青面层，使之形成整体。目前针对不粘轮，市场上有不粘轮粘层油。这种不粘轮粘层油只是提高粘层油的软化点，但是并没有注意其粘接强度。而且，生产工艺复杂，不容易生产，因此并没有大力推广使用，而且售价高，产品性价比极低。
技术实现思路
本专利技术要解决的技术问题是提供一种生产工艺步骤简单，粘结强度高，且不粘轮的高黏不粘轮粘层油。为了解决上述技术问题，本专利技术的技术方案为：一种高黏不粘轮粘层油，由下列重量比例的各组分组成：基质沥青：有机高分子化合物：橡胶油：植物油酸＝60～90：5～15：2～8：9～18。作为优选，所述的有机高分子化合物为常温液态。作为优选，所述的高黏不粘轮粘层油固含量大于60％，软化点大于70℃，粘接强度本文档来自技高网...

【技术保护点】
1.一种高黏不粘轮粘层油，其特征在于：由下列重量比例的各组分组成：基质沥青：有机高分子化合物：橡胶油：植物油酸＝60～90：5～15：2～8：9～18。

【技术特征摘要】
1.一种高黏不粘轮粘层油，其特征在于：由下列重量比例的各组分组成：基质沥青：有机高分子化合物：橡胶油：植物油酸＝60～90：5～15：2～8：9～18。2.如权利要求1所述的高黏不粘轮粘层油，其特征在于：所述的有机高分子化合物为常温液态。3.如权利要求1所述的高黏不粘轮粘层油，其特征在于：所述的高黏不粘轮粘层油固含量大于60％，软化点大于70℃，粘接强度为1....

【专利技术属性】
技术研发人员：许慧，谢钱清，陈娟，
申请(专利权)人：陈娟，
类型：发明
国别省市：江苏,32