The invention discloses a high toughness anti-cracking cable material and a preparation method thereof. The cable material is made of 30 45 parts of nitrile butadiene rubber, 20 30 parts of linear low density polyethylene, 15 25 parts of ethylene-methyl acrylate copolymer, 5 10 parts of polypropylene fiber, 5 10 parts of nano titanium dioxide, 8 16 parts of flame retardant, 6 15 parts of filler and 4 10 parts of antioxidant. One part, softener 12 25 parts, cross-linking agent 2 6 parts and assistant cross-linking agent 0.5 2 parts. The cable material with high toughness and crack resistance has good toughness, crack resistance, excellent high temperature resistance, oil resistance and aging resistance.
【技术实现步骤摘要】
一种高韧性抗开裂电缆料及其制备方法
本专利技术属于高分子材料
，具体涉及一种高韧性抗开裂电缆料及其制备方法。
技术介绍
随着经济的迅速发展，电缆在通讯、电力等领域的应用非常广泛，当电缆在高温环境下使用时，现有电缆表面电缆料会出现开裂现象，导致电缆的折断和传输信号的中断，将会严重影响人们的正常生活。公开号为CN108410045A的中国专利申请公开了一种耐高温的阻燃无毒电缆料。电缆料中包括如下组分：聚烯烃类热塑性弹性体、聚氨酯弹性体橡胶、三元乙丙橡胶、陶粉、偏苯三酸三辛酯、硬脂酸锌、增强剂、纳米二氧化硅、硅烷偶联剂、阻燃剂、抑烟剂和抗氧剂。其中，陶粉是由凹凸棒石粘土、蒙脱土、海泡石等材料经过改性、煅烧和研磨后得到粉末。聚氨酯弹性体橡胶为聚己内酯型的热塑性聚氨酯弹性体橡胶，增强剂为高耐磨炭黑；阻燃剂为纳米二氧化铝、纳米二氧化镁和氧化锑的混合物，混合物中三者的质量比2:4:3；抑烟剂为硼酸锌、三氧化钼和有机改性蒙脱土中的一种。该型电缆料的耐高温性能突出，并且具有良好的阻燃性能，非常绿色安全。但是，该专利聚烯烃类热塑性弹性体用量大，影响电缆料的强度。公开号为1084...
【技术保护点】
1.一种高韧性抗开裂电缆料，其特征在于，由以下重量份数的原料制成：丁腈橡胶30‑45份，线性低密度聚乙烯20‑30份，乙烯‑丙烯酸甲酯共聚物 15‑25份，聚丙烯纤维5‑10份，纳米二氧化钛5‑10份，阻燃剂8‑16份，填充剂6‑15份，防老剂4‑10份，软化剂12‑25份，交联剂2‑6份和助交联剂0.5‑2份。
【技术特征摘要】
1.一种高韧性抗开裂电缆料，其特征在于，由以下重量份数的原料制成：丁腈橡胶30-45份，线性低密度聚乙烯20-30份，乙烯-丙烯酸甲酯共聚物15-25份，聚丙烯纤维5-10份，纳米二氧化钛5-10份，阻燃剂8-16份，填充剂6-15份，防老剂4-10份，软化剂12-25份，交联剂2-6份和助交联剂0.5-2份。2.根据权利要求1所述的高韧性抗开裂电缆料，其特征在于，所述的阻燃剂为三氧化二锑、氢氧化镁、氧化铝、氧化锌和硼酸锌中一种或几种。3.根据权利要求1所述的高韧性抗开裂电缆料，其特征在于，所述的填充剂为轻质碳酸钙、炭黑N330、炭黑N550和炭黑N660中一种或几种。4.根据权利要求1所述的高韧性抗开裂电缆料，其特征在于，所述的防老剂为OD、MB和4010NA中一种或几种。5.根据权利要求1所述的高韧性抗开裂电缆料，其特征在于，所述的软化剂为二甲基硅油或者羟基硅油。6.根据权利要求1所述的高韧性抗开裂电缆料，其特征在于，...
【专利技术属性】
技术研发人员：常雪梅，赵世鑫，陈婧媛，常雪松，陈峰，张颖，王维新，
申请(专利权)人：国网河南省电力公司方城县供电公司，
类型：发明
国别省市：河南,41