A magnetic activated carbon adsorbing material and its preparation method were prepared by impregnating and activating grapefruit peel with phosphoric acid to prepare activated grapefruit peel-based biomass. On this basis, magnetic activated carbon was prepared by doping magnetic material iron. Through infrared spectrum analysis of biomass charcoal, it is found that there are a large number of oxygen-containing functional groups on its surface, such as hydroxyl, C H, carbonyl, etc., and it has aromatic ring structure, forming favorable conditions for adsorption. The prepared biochar is loaded and magnetized to prepare magnetic biochar materials, and then the adsorbent is quickly and effectively separated from the solution by using magnetic materials. It is conducive to desorption and regeneration.
【技术实现步骤摘要】
一种磁性活化炭吸附材料及制备方法
本专利技术涉及一种吸附性材料,具体的说是一种磁性活化炭吸附材料及制备方法。
技术介绍
生物炭是厌氧条件下,将生物质经过高温热解后生成的含碳固体。制备生物炭的原料极为丰富,植物性、矿物性等含碳物质均可用于制备生物炭。该种物质含有60%以上的碳,其余为H、O、N、S及一些微量元素。除具有高比表面积外,表面官能团十分丰富,包含羧基、酚羟基、酸酐等多种基团,还含有大量的负电荷以及较高的电荷密度,化学和生物学稳定性很高,可溶性极低。生物炭的这些基本性质使其具有吸附性能、催化性能和抗生物分解能力,对金属离子及有机化合物具有很高的吸附能力,在农业、能源、环境等领域都有广泛的应用。我国生物质资源丰富、种类多样,近年来在国家大力发展绿色经济、提倡可持续发展的理念下,有越来越多的学者把农林生物质作为生产生物炭的原料[3,5],使得这些废弃物不再以简单的填埋、焚烧等方式处理,减轻对环境的污染,变废为宝,更充分、合理的利用资源。另一方面,生物炭及改性生物炭粉末较细,实际应用时较难从溶液体系中分离,对其脱附再生有很大的影响,因此本申请将所制备的生物炭进行负 ...
【技术保护点】
1.一种磁性活化炭吸附材料的制备方法,其特征在于,包括如下步骤:步骤一,柚子皮洗净、晒干;步骤二,粉碎机进行破碎、球磨机球磨、研钵研磨,分别用80~200目的筛子进行筛分;步骤三,将筛分后的粉末称取一定的质量放入烧杯中,按质量比1:1~2用磷酸浸渍,搅拌均匀后,静置8~24小时;步骤四,浸渍后过滤掉上层液体,将固体样品水洗多次,放入烘箱烘干后磨碎,制备活化柚子皮基生物质;将氧化铁加入该生物质中,分别在300℃~700℃下放入管式炉,通氩气隔绝氧气高温煅烧1~2小时,保温1~2小时,制备磁性活化炭吸附材料。
【技术特征摘要】
1.一种磁性活化炭吸附材料的制备方法,其特征在于,包括如下步骤:步骤一,柚子皮洗净、晒干;步骤二,粉碎机进行破碎、球磨机球磨、研钵研磨,分别用80~200目的筛子进行筛分;步骤三,将筛分后的粉末称取一定的质量放入烧杯中,按质量比1:1~2用磷酸浸渍,搅拌均匀后,静置8~24小时;步骤四,浸渍后过滤掉上层液体,将固体样品水洗多次,放入烘箱烘干后磨碎,制备活化柚子皮基生物质;将氧化铁加入该生物质中,分别在300℃~700℃下放入管式炉,通氩气隔绝氧气高温煅烧1~2小时,保温1...
【专利技术属性】
技术研发人员:李倩,张宇,黄青,任欢杰,黎红文,
申请(专利权)人:湖北第二师范学院,
类型:发明
国别省市:湖北,42