Electroplating Solution for Diamond Cutting Line

The present invention relates to an electroplating solution for diamond cutting line. Its solutes include 600-1000g/L nickel sulfamate, 35-45g/L boric acid, 0.1-0.5ml/L polyethylene glycol 8000, 0.1-0.5ml/L Jimmy quaternary ammonium salt, 1-10g/L diamond powder, and its solvent is water. The diamond cutting line made from the electroplating solution has stable diamond particles, not easy to fall off, uniform metal coating, high hardness of the coating, strong diamond control, large effective cutting surface, remarkable improvement of cutting efficiency and cutting ability, and effective reduction of the cost of producing diamond cutting line.

【技术实现步骤摘要】
金刚石切割线的电镀溶液
本专利技术属于电镀
，具体涉及一种金刚石切割线电镀溶液。
技术介绍
太阳能光伏发电是目前快速发展的可持续能源利用形式之一，近年来在美国、欧盟、日本以及中国都得到了迅速发展。目前光伏发电应用最广的是晶体硅太阳能电池。降低太阳能发电成本一直是光伏行业的发展目标。硅锭开放截断需要使用金刚石切割线进行切割截断，而金刚石切割线的切割寿命直接影响发电的成本。传统的镀镍方式是把金刚石颗粒固定在不锈钢条表面上，形成切割线但是由于镍的硬度偏小，对金刚石的把持力不够，切割使用过程中金刚石颗粒容易脱落而导致失去切割能力。并且由于镀镍溶液分散性较差，在刃口处的金属镀层厚度不均匀，有厚有薄，刃口上部分金刚石由于埋入率太小导致使用时容易脱落。部分由于镀层过厚导致金刚石埋入率过高，大大减弱刀刃的有效切割面积，致使切割能力变差。金刚石切割线切割寿命短，造成截断硅材料成本高。
技术实现思路
本专利技术的目的在于提供一种金刚石切割线的电镀溶液，该电镀溶液能够令金刚石切割线的金刚石颗粒稳固，不易脱落，金属镀层均匀、镀层硬度高，把持金刚石的力度大，有效切割面大，切割效率及切割能力显著提高。本专利技本文档来自技高网...

【技术保护点】
1.一种金刚石切割线的电镀溶液，其特征在于，包括如下浓度的各溶质：氨基磺酸镍，600～1000g/L；硼酸，35～45g/L；聚乙二醇8000，0.1～0.5ml/L；吉米奇季铵盐，0.1～0.5ml/L；金刚石微粉，1～10g/L；所述电镀液的溶剂为水。

【技术特征摘要】
2018.08.23 CN 20181096342311.一种金刚石切割线的电镀溶液，其特征在于，包括如下浓度的各溶质：氨基磺酸镍，600～1000g/L；硼酸，35～45g/L；聚乙二醇8000，0.1～0.5ml/L；吉米奇季铵盐，0.1～0.5ml/L；金刚石微粉，1～10g/L；所述电镀液的溶剂为水。2.如权利要求1所述的金刚石切割线的电镀溶液，其特征在于，各溶质的浓度为：氨基磺酸镍，600g/L；硼酸，35g/L；聚乙二醇8000，0.1ml/L；吉米奇季铵盐，0.1ml...

【专利技术属性】
技术研发人员：郑建国，罗小平，
申请(专利权)人：信丰崇辉科技有限公司，
类型：发明
国别省市：江西,36