The invention discloses a method for preparing magnesium phosphate/Super P composite corrosion resistant coating, which belongs to the field of surface electroplating of Nd-Fe-B permanent magnet material. The method of the invention is: alkali washing and oil removing of Nd-Fe-B matrix, acid washing and rust removing, sandpaper grinding, and then electrodeposition. The composition and content of the electrolyte are magnesium oxide 2-3 g/L, phosphoric acid 10-15 g/L, Super_P 200-250 mg/L, surfactant 50-55 mg/L. The method of the invention is simple, environmentally friendly and pollution-free, and the obtained coating is thicker, uniform and compact, and has good adhesion. Adding Super P can obviously improve the corrosion resistance of the coating and protect the Nd-Fe-B matrix.
【技术实现步骤摘要】
一种制备磷酸镁/Super-P复合耐蚀涂层的方法
本专利技术涉及一种制备磷酸镁/Super-P复合耐蚀涂层的方法，钕铁硼永磁材料表面电镀领域。
技术介绍
钕铁硼磁体由于具有良好的磁性能和性价比而被认为是第三代稀土永磁体，但是，由于这类材料具有多相结构，从而导致其在大部分环境中耐腐蚀性能比较差；这一缺陷极大的制约了其产业的发展。国内外已经很多人做了关于提高钕铁硼永磁体材料的耐腐蚀性能研究，例如合金化法和镀层防护法；研究表明，添加合金元素能够促进在晶界处形成金属间化合物，可以改善磁体晶间相的电位，从而提高钕铁硼磁体的耐腐蚀性。但是添加合金元素，会导致磁体的磁性能降低。Co等合金元素在晶界形成了化合物，可以减少了晶界相的反应活性，但这些非磁性相的形成，会降低磁体的磁能积和矫顽力，导致磁体的磁性能降低。镀层防护法是提高钕铁硼磁体耐蚀性最主要的方法，同时也是实际应用最有效的抗腐蚀手段。中国专利技术专利，申请号：201210481482.8，进行了提高钕铁硼永磁体表面磷化膜耐蚀性的研究，其磷化液组成较为复杂，不易操作，磷化时间较长，且得到磷化膜厚度较薄。
技术实现思路
本专利技术...
【技术保护点】
1.一种制备磷酸镁/Super‑P 复合耐蚀涂层的方法，其特征在于：对钕铁硼基体进行碱洗除油，酸洗除锈，砂纸打磨，然后进行电沉积，其中电解液的组成及含量为：氧化镁 2~3g/L、磷酸10~15g/L、Super‑P 200~250mg/L、表面活性剂 50~55mg/L。
【技术特征摘要】
1.一种制备磷酸镁/Super-P复合耐蚀涂层的方法，其特征在于：对钕铁硼基体进行碱洗除油，酸洗除锈，砂纸打磨，然后进行电沉积，其中电解液的组成及含量为：氧化镁2~3g/L、磷酸10~15g/L、Super-P200~250mg/L、表面活性剂50~55mg/L。2.根据权利要求1所述制备磷酸镁/Super-P复合耐蚀涂层的方法，其特征在于：电沉积的条件为：PH值为4.4~4.6，电流密度为5mA/cm2，时间为15~20min，温度为50~80℃。3.根据权利要求1所述制备磷酸镁/Super-P复合耐蚀涂层的方法，其特征...