The invention discloses an epoxy acrylic resin flame retardant paint and a preparation method thereof. The paint comprises the following raw materials: epoxy acrylate prepolymer 20 40, flame retardant 15 40, initiator 0.5 1.5, pigment 4 10, dispersant 1.5 3.5, inorganic filler 4 10, defoamer 2 5, film forming additive 2 6, solvent 5 30. By adding reactive flame retardant to the matrix resin, the flame retardant and the acrylate prepolymer form a completely compatible whole, so that the prepared flame retardant coating not only has excellent and lasting flame retardant effect, but also has excellent physical and mechanical properties, water resistance, chemical corrosion resistance and high bonding strength.
【技术实现步骤摘要】
一种环氧丙烯酸树脂阻燃涂料及其制备方法
本专利技术属于涂料领域，具体涉及一种环氧丙烯酸树脂阻燃涂料及其制备方法。
技术介绍
阻燃涂料就是通过将涂料刷在易燃材料的表面，平时可起到一定的装饰作用，一旦发生火灾，则能够减缓火焰蔓延传播速度，在一定时间内阻止燃烧，达到保护基材、使人们又足够的时间离开火场和组织抢救的目的。阻燃涂料的防火原理大致可归纳为以下五点：(1)防火涂料本身具有难燃性或不燃性，使被保护基材不直接与空气接触，延迟物体着火和减少燃烧的速度；(2)防火涂料除本身具有难燃性或不燃性外，它还具有较低的导热系数，可以延迟火焰温度向被保护基材的传递；(3)防火涂料受热分解出不燃惰性气体，冲淡被保护物体受热分解出的可燃性气体，使之不易燃烧或燃烧速度减慢；(4)含氮的防火涂料受热分解出NO、NH3等基团，与有机游离基化合，中断连锁反应，降低温度；(5)膨胀型防火涂料受热膨胀发泡，形成碳质泡沫隔热层封闭被保护的物体，延迟热量与基材的传递，阻止物体着火燃烧或因温度升高而造成的强度下降。环氧丙烯酸酯树脂是一类非常重要的基体树脂，因其分子中含有环氧基、醚键等活性基团，可以改善涂...
【技术保护点】
1.一种环氧丙烯酸树脂阻燃涂料，其特征在于，按重量百分比计，所述涂料包括以下原料：
【技术特征摘要】
1.一种环氧丙烯酸树脂阻燃涂料，其特征在于，按重量百分比计，所述涂料包括以下原料：2.根据权利要求1所述的一种环氧丙烯酸树脂阻燃涂料，其特征在于，所述环氧丙烯酸酯预聚物为由环氧树脂和丙烯酸酯单体的聚合物，在向环氧树脂体系通入氮气保护并搅拌的条件下，将所述环氧树脂体系升温至50-70℃时缓慢滴加所述丙烯酸酯单体，控制在1-1.5h内滴完，滴加完毕后将体系温度升温至80-90℃，恒温反应2-3h，冷却至室温出料，即制得所述环氧丙烯酸酯预聚物。3.根据权利要求1所述的一种环氧丙烯酸树脂阻燃涂料，其特征在于，所述阻燃剂包括以下组分：丙炔酸类单体、五溴苯酚和溴水；将所述丙炔酸类单体与所述五溴苯酚在浓硫酸的催化下反应得到丙炔酸五溴苯酚酯，将所述丙炔酸五溴苯酚酯与溴水反应得到所述阻燃剂。4.根据权利要求1的一种环氧丙烯酸树脂阻燃涂料，其特征在于，所述引发剂为过氧化苯甲酰、过氧化3,3,5-三甲基己酸叔丁酯和过氧化醋酸叔戊酯中的一种或多种。5.根据权利要求1所述...
【专利技术属性】
技术研发人员：谭贺洵，汪洋，曾志伟，
申请(专利权)人：广东鑫皇冠新材料有限公司，
类型：发明