The invention discloses a reactive ambient temperature color asphalt, a preparation method and application thereof. The reactive ambient temperature color asphalt of the invention comprises 50 to 60 weight parts of petroleum resin, 20 to 30 weight parts of reactive solvent, 10 to 20 weight parts of coupling agent, 10 to 20 weight parts of waterborne epoxy resin and 2 to 5 weight parts of pigments. The reactive normal temperature color asphalt of the invention reduces the heating process of asphalt before construction and paving of color asphalt mixture, and the heating process of aggregate, so the construction is simpler, more energy-saving and more environmental protection. In addition, the normal temperature color asphalt is ready to be used, which has a wider scope of application.
【技术实现步骤摘要】
反应型常温彩色沥青及其制备方法和用途
本专利技术涉及沥青路面材料领域，特别涉及反应型常温彩色沥青及其制备方法和用途。
技术介绍
随着近年来，人们对审美的要求在不断提高，对道路的美观或功能区分的要求也日渐凸显。彩色沥青作为一种常见的路面材料，由于其颜色多样、色彩亮丽等特点，主要用于公园、景区道路、绿道、自行车道，具有美观、醒目以及视觉引导等优点。目前彩色沥青的制备方法包括：1)普通沥青经脱色后再染色；2)使用石油树脂作为主要胶结料，由于石油树脂颜色浅，因而可以直接使用颜料进行着色。上述第一种方法由于需要对黑色沥青进行脱色，工艺复杂，且效果不佳，故而已经弃用；而第二种方法中，石油树脂的粘性和熔点高，通常需要加热到170-180℃后再与同样加热的集料进行拌合，制备工艺复杂，且耗能严重。针对上述存在的制备工艺复杂，能耗高的问题，CN105778529A公开了一种温拌型彩色沥青胶结料的制备方法，由彩色沥青胶结料和RSA型改性剂组成，其中所述RSA型改性剂为氧化聚乙烯，由分子量为2000-2500的线性低密度聚乙烯氧化而成；所述温拌型彩色沥青胶结料中RSA型改性剂的掺入量以重...
【技术保护点】
1.一种反应型常温彩色沥青，其包含50‑60重量份的石油树脂、20‑30重量份反应型溶剂、10‑20重量份偶联剂、10‑20重量份水性环氧树脂和2‑5重量份颜料。
【技术特征摘要】
1.一种反应型常温彩色沥青，其包含50-60重量份的石油树脂、20-30重量份反应型溶剂、10-20重量份偶联剂、10-20重量份水性环氧树脂和2-5重量份颜料。2.根据权利要求1所述的反应型常温彩色沥青，其中所述颜料包括氧化铁红、氧化铁黄和氧化钴。3.根据权利要求1所述的反应型常温彩色沥青，其中所述反应型溶剂包含15-25重量份不饱和脂肪酸、5-10重量份烷基二甲基甜菜碱和0.5-5重量份苯酚多聚物。4.根据权利要求1所述的反应型常温彩色沥青，其中所述偶联剂为C10-C20烷基三乙氧基硅烷。5.根据权利要求3所述的反应型常温彩色沥青，其中所述不饱和脂肪酸、所述烷基二甲基甜菜碱和所述苯酚多聚物的重量比为10:2-3:0.5-1。6.根据权利要求3所述的反应型常温彩色沥青，其中所述不饱和脂肪酸选自肉豆蔻油酸、棕榈油酸、反式油酸、蓖麻油酸、油酸、亚油酸和芥酸组成的组中的至少一种；所述烷基二甲基甜菜碱为C10-C20烷基二甲基甜菜碱；所述苯酚多聚物为三-(二甲胺基甲基)苯酚多聚物。7.一种根...
【专利技术属性】
技术研发人员：李九苏，王潇潇，沈增晖，张毅，
申请(专利权)人：湖南鑫长胜材料科技有限公司，
类型：发明
国别省市：湖南,43